Credibility ,410 stainless steel is a martensitic stainless steel that provides good corrosion resistance plus high strength and hardness. It is magnetic in both the annealed and hardened conditions. A wide of properties can be achieved with different heat treatments. Applications requiring moderate corrosion resistance and high mechanical properties are ideal for this alloy.
Stainless steel pipe fittings, hardware, stainless steel bars, stainless steel compressor parts, valve parts for oil fields, stainless steel fasteners, springs, pins, stainless steel flanges, stainless steel pipes.
Element | Weight % |
C | 0.15 |
Mn | 1.00 |
Si | 1.00 |
Cr | 11.5-13.0 |
P | 0.04 |
S | 0.03 |
Properties | Conditions | ||
T (°C) | Treatment | ||
Density (×1000 kg/m3) | 7.8 | 25 | |
Poisson's Ratio | 0.27-0.30 | 25 | |
Elastic Modulus (GPa) | 200 | 25 | |
Tensile Strength (Mpa) | 485 | 25 | annealed, hot finished (wire) more |
Yield Strength (Mpa) | 275 | ||
Elongation (%) | 20 | ||
Reduction in Area (%) | 45 | ||
Hardness (HRB) | 95 (max) | 25 | annealed (plate, sheet, strip) |
Properties: Annealed
Ultimate Tensile Strength: 65 KSI min (450 MPa min)
Yield Strength (0.2% offset): 30 KSI min (205 MPa min)
Elongation: 20% min
Hardness: Rb 88 max
Corrosion Resistance
Finishes
# 1 –Hot rolled annealed and descaled. It is available in strip, foil and ribbon. It is used for applications where a smooth decorative finish is not required.
# 2D – Dull finish produced by cold rolling, annealing and descaling. Used for deep drawn parts and those parts that need to retain lubricants in the forming process.
# 2B –Smooth finish produced by cold rolling, annealing and descaling. A light cold rolling pass is added after anneal with polished rolls giving it a brighter finish than 2D.
#BA – Bright annealed cold rolled and bright annealed
#CBA – Course bright annealed cold rolled matte finish and bright anneal
#2 – Cold Rolled
# 2BA – Smooth finish produced by cold rolling and bright annealing. A light pass using highly polished rolls produces a glossy finish. A 2BA finish may be used for lightly formed applications where a glossy finish is desired in the formed part.
Polished – Various grit finish for specific polish finished requirements
Wire Finishes
XC – Extra clean, bright annealed or bright annealed and cold rolled
Grease – Ultra bright finish for decorative applications
Soap – Soap is not removed from tempered wire to act as a lubricant.
Heat Treatment
410 stainless steel can be hardened by cold working and by heat treating.
Source: Yaang Pipe Industry Co., Limited (www.yaang.com)
Tel No:+86-18267732328 / Email:[email protected]
Address:Longwan District, Wenzhou, Zhejiang Province, China.
Copyright Notice © www.yaang.com Yaang Pipe Industry Co., Limited All rights reserved.
Yaang Pipe Industry Co., Ltd. is an international supplier of piping solutions for flange, butt welding fittings, socket welding fittings and threaded fittings. Our products are widely used in different industrial fields, including oil and gas, chemical industry, petrochemical industry, power plant, pulp and paper industry, environmental and water conservancy engineering, engineering projects, etc.