Stainless Steel 409 (UNS S40900)

Yaang Stainless inventory includes Alloy 409 (UNS S40900) in  Stainless Steel Pipes.  Other product forms such as Stainless Steel Flanges, Stainless Steel Pipe Fittings.

Overview

General Properties

Alloy 409 is a general purpose, chromium, titanium stabilized, ferritic stainless steel whose primary application is automotive exhaust systems. It contains 11% chromium which is the minimum amount for the formation of the passive surface film which gives stainless steels their corrosion resistance. It combines good elevated temperature corrosion resistance with medium strength, good formability, and overall cost. Alloy 409 resists corrosion strongly compared to carbon steel and is used as an alternative to carbon steel in mildly challenging environments where its high resistance to corrosion and high temperature oxidation gives an advantage. It is commonly used in applications where appearance is a secondary quality to mechanical properties and corrosion resistance.

Applications:

Although Alloy 409 is designed principally for the automotive exhaust industry, it has been successfully used in other industrial applications as well. Some examples of applications that call for Alloy 409 include:

• Automotive exhaust systems
• Catalytic converters
• Mufflers
• Tailpipes
• Farm equipment
• Structural support and hangers
• Transformer cases
• Furnace components
• Heat exchanger tubing

Standards:

• ASTM/ASME: UNS S40900
• EURONORM: FeMi35Cr20Cu4Mo2
• DIN: 2.4660

Resistance

Corrosion Resistance:

• Resists atmospheric and exhaust gas corrosion
• In most atmospheres a light surface rust will form which inhibits further corrosion but makes the surface less appealing

 Heat Resistance

• Generally classified as resistant to scaling in intermittent service up to 1499^oF (815^oC ) and up to 1247^oF (675^oC) in continuous service

Processing

Weldability

• Readily weldable
• Pre-heat of 302 to 500^oF (150 to 260^oC) is recommended
• Post-weld annealing at 1400 to 1499^oF improved weld ductility
• Post-weld annealing is not required when welding thin sections
• Automotive exhaust tubing is typically welded without filler metal

Properties

Chemical Properties:

	C	Mn	Si	P	S	Cr	Ni	Ti
409	max:0.08	max:1.0	max:1.0	max:0.045	max: 0.045	min: 10.5 max: 11.75	max: 0.5	min: 0.48  max: 0.75

Mechanical Properties:

Grade	Tensile Strength MPa (min)	Yield Strength 0.2% MPa(min)	Elongation %	Hardness (Brinell) MAX	Hardness (Rockwell B) MAX
409	380	207	20	207	95

Physical Properties:

Density lbm/in3	Thermal Conductivity (BTU/h ft. °F)	Electrical Resistivity (in x 10-6)	Modulus of Elasticity (psi x 106	Coefficient of Thermal Expansion (in/in)/ °F x 10-6	Specific Heat (BTU/lb/ °F)	Melting Range (°F)
at 68°F: 0.280	9.4 at 212°F	28.3 at 68°F	29	5.84 at 32 – 212°F	0.114 at 68°F to 212°F	2500 to 2590
	12.4 at 932 °F	39.4 at 752°F		6.60 at 32 – 1000°F
		49.6 at 1652 °F		6.86 at 32 – 1500°F