- SITEMAP
- CONTACT US
- 8618267732328
News
Credibility ,the lifeblood of enterprise!
- Fittings
- Butt Welding Fittings
- Forged Fittings
- 180 Degree Elbows
- 90 Degree Elbows
- 60 Degree Elbows
- 45 Degree Elbows
- 30 Degree Elbows
- Equal Tee
- Reducing Tee
- Concentric Reducer
- Eccentric Reducer
- Lap Joint Stub End
- Outlets
- Cap
- Bend
- Cross
- Coupling
- Stainless Steel Lateral Tee
- Bellows Expansion Joints
- Flexible Metal Hose
- Non-Standard/Custom Fittings
- Bleed & Flushing Rings
- Types of Flanges
- Anchor Flanges
- Blind Flanges
- Expander Flanges
- High Hub Flanges
- Lap Joint Flanges
- Long Weld Neck Flanges
- Nipoflanges
- Orifice Flanges
- Plate Flanges
- Ring Type Joint Flanges
- Reducing Flanges
- Slip On Flanges
- Socket Weld Flanges
- Spectacle Blind Flanges
- Square Flanges
- Spades & Ring Spacers
- Threaded Flanges
- Welding Neck Flanges
Stainless Steel 420 (UNS S42000)
Yaang Stainless inventory includes Alloy 420 (UNS S42000) in Stainless Steel Pipes. Other product forms such as Stainless Steel Flanges, Stainless Steel Pipe Fittings.
Overview
General Properties
Alloy 420 is a hardenable, martensitic stainless steel that is a modification of Alloy 410. Similar to 410, it contains a minimum of 12% chromium, just sufficient enough to give corrosion resistant properties. Alloy 420 has higher carbon content than Alloy 410 which is designed to optimize strength and hardness characteristics. It has good ductility it the annealed condition but is capable of being hardened up to Rockwell hardness 50 HRC, the highest hardness of the 12% chromium grades. Due to its hardening properties, Alloy 420 is not often welded, although it is possible. Martensitic stainless steels are designed for high hardness and sometimes other properties are to some degree compromised. Corrosion resistance is lower than the common austenitic grades and their useful operating range is limited by their loss of ductility at sub-zero temperatures and loss of strength by over-tempering at elevated temperatures. Its best corrosion resistance is achieved when the metal is hardened and surface ground or polished.
Specifications: UNS S42000
Applications:
Alloy 420 is used for a variety of applications where good corrosion and outstanding hardness is necessary. It is not usually used at temperatures exceeding 800oF (427oC) due to quick hardening and loss of corrosion resistance. Examples of applications that use alloy 420 include:
- Cuttery
- Knife blades
- Surgical instruments
- Needle valves
- Shear blades
- Scissors
- Hand tools
Standards:
- ASTM/ASME: UNS S42000
- EURONORM: FeMi35Cr20Cu4Mo2
- DIN: 2.4660
Resistance
Corrosion Resistance:
- Less resistant than the austenitic grades and the 17% chromium ferritic alloys
- Good resistance in the hardened condition to the atmosphere, foods, fresh water, and mild acids
- Resistance lowered in the annealed condition
- Best with a smooth surface finish
Heat Resistance:
- Not recommended for use above the relevant tempering temperature because of reduction in mechanical properties
- Scaling temperature is approximately 1202oF (650oC)
Processing
Machinability
- Tough, stringy chip build-up.
- Similar to machining some of the high carbon tool steel
Welding
- Not commonly welded due to air hardening characteristics.
- Welding may be performed after preheating to 300-400 F
- Post weld tempering at temperature for 2 hours
Hot Working
- Recommended to bring temperatures slowly up to 1400, then on to 2000-2200 F
- Furnace cool slowly to avoid cracking, after furnace working
- Reheating is necessary to keep working temperature above 1600 F.
Cold Working
- Can withstand only minor cold work.
- Radical forming operations will result in cracking.
Annealing
- Anneal at temperatures between 1550-1650 F (843-900 C)
- Allow for slow furnace cooling.
Tempering
- Temper at temperatures of 300-400 F
- Air cool for maximum hardness and corrosion resistance.
Hardening
- Soak at 1850-1950 F to quench in heated oil.
Properties
Chemical Properties:
| C | Mn | Si | P | S | Cr | |
|---|---|---|---|---|---|---|
| 420 | 0.15 max |
1.00 max |
1.00 max |
0.04 max |
0.03 max |
min: 12.0 max: 14.0 |
Mechanical Properties:
| Tempering Temperature (°C) | Tensile Strength (MPa) | Yield Strength 0.2% Proof (MPa) |
Elongation (% in 50mm) |
Hardness Brinell (HB) |
|---|---|---|---|---|
| Annealed * | 655 | 345 | 25 | 241 max |
| 399°F (204°C) | 1600 | 1360 | 12 | 444 |
| 600°F (316°C) | 1580 | 1365 | 14 | 444 |
| 800°F (427°C) | 1620 | 1420 | 10 | 461 |
| 1000°F (538°C) | 1305 | 1095 | 15 | 375 |
| 1099°F (593°C) | 1035 | 810 | 18 | 302 |
| 1202°F (650°C) | 895 | 680 | 20 | 262 |
| * Annealed tensile properties are typical for Condition A of ASTM A276; annealed hardness is the specified maximum. | ||||
Physical Properties:
| Density kg/m3 |
Thermal Conductivity W/mK |
Electrical Resistivity (Microhm/cm) |
Modulus of Elasticity |
Coefficient of Thermal Expansion µm/m/°C |
Specific Heat (J/kg.K) |
|---|---|---|---|---|---|
| 7750 | 24.9 at 212°F | 550 (nΩ.m) at 68°F | 200 GPa | 10.3 at 32 – 212°F | 460 at 32°F to 212°F |
| – at 932 °F | 10.8 at 32 – 599°F | ||||
| 17.7 at 32-1000°F |
Tel No：+86-18267732328 / Email:[email protected]
Address：Longwan District, Wenzhou, Zhejiang Province, China.
Copyright Notice © www.yaang.com Yaang Pipe Industry Co., Limited All rights reserved.
Yaang Pipe Industry Co., Ltd. is an international supplier of piping solutions for flange, butt welding fittings, socket welding fittings and threaded fittings. Our products are widely used in different industrial fields, including oil and gas, chemical industry, petrochemical industry, power plant, pulp and paper industry, environmental and water conservancy engineering, engineering projects, etc.