Home > Alloy steel > ASTM 13Q


ASTM 13Q angle bars, ASTM 13Q flanges, Pipe Fitting, Steel Pipe, Heat Exchanger and Reducer, Gasket, Tee, Pipe Fitting, Tube Plate, have all specifications. With many yeas production experience, strict control ASTM 13Q chemical composition and ASTM 13Q mechanical properties.

Production specification
Data center describes many of the common steel models, we can not determine the company's warehouse has all types of steel products inventory or raw materials.

Angle bar: 1mm to 1300mm
Steel Pipe: 1 - 1300mm, also can be customed.
Pipe fitting Size: 1/8 inch - 80 inch (DN6 - DN2000)
Flange Size: DN6 - DN2000
Lenth: Any lenth based on the customer's requirement.


Data Table for:Products: Alloy steel:ASTM 13Q

ASTM 13Q properties and heat treatment forged piece, Including ASTM 13Q application and specifications, Including ASTM 13Q tube plate, ASTM 13Q tube sheet, ASTM 13Q Pipe fittings, ASTM 13Q flat bar,ASTM 13Q Valve,ASTM 13Q forgings.

ASTM 13Q has the following specifications:

Chemical composition % of the ladle analysis of grade ASTM 13Q and Standards

Cr Ni
0.15-0.25 0.2-0.8 0.65-0.95 0.04 0.045 0.4-0.7 0.4-0.7
Mo Al Cu Nb Ti W V
0.15-0.25   0.5     0.1  

Machining performance

ASTM 13Q the mechanical properties of the report, the report provides detailed performance analysis and application.

Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.

Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.

Hot tags:ASTM 13Q steel plate, ASTM 13Q sheet, ASTM 13Q Pipe fittings, ASTM 13Q flat bar,ASTM 13Q Valve,ASTM 13Q heat exchanger parts

Related hot word search:ASTM 13Q Valve ASTM 13Q,forging ASTM 13Q,ASTM 13Q tube sheet,elbow ASTM 13Q,ASTM 13Q flat bar,pipe ASTM 13Q,ASTM 13Q Tee

Prev:ICI 8620
Next:ICI 6150