ICI 4330

ICI 4330 angle bars, ICI 4330 flanges, Pipe Fitting, Steel Pipe, Heat Exchanger and Reducer, Gasket, Tee, Pipe Fitting, Tube Plate, have all specifications. With many yeas production experience, strict control ICI 4330 chemical composition and ICI 4330 mechanical properties.

Production specification
Data center describes many of the common steel models, we can not determine the company's warehouse has all types of steel products inventory or raw materials.

Angle bar: 1mm to 1300mm
Steel Pipe: 1 - 1300mm, also can be customed.
Pipe fitting Size: 1/8 inch - 80 inch (DN6 - DN2000)
Flange Size: DN6 - DN2000
Lenth: Any lenth based on the customer's requirement.

ICI 4330

Data Table for:Products: Alloy steel:ICI 4330

ICI 4330 properties and heat treatment forged piece, Including ICI 4330 application and specifications, Including ICI 4330 tube plate, ICI 4330 tube sheet, ICI 4330 Pipe fittings, ICI 4330 flat bar,ICI 4330 Valve,ICI 4330 forgings.

ICI 4330 has the following specifications:


Chemical composition % of the ladle analysis of grade ICI 4330 and Standards

C
Si
Mn
P
S
Cr Ni
0.25-0.35 0.2-0.8 0.4-0.7 0.04 0.045 0.7-0.9 1.65-2.0
Mo Al Cu Nb Ti W Ce
0.2-0.3   0.5     0.1  



Machining performance

ICI 4330 the mechanical properties of the report, the report provides detailed performance analysis and application.


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.



Hot tags:ICI 4330 steel plate, ICI 4330 sheet, ICI 4330 Pipe fittings, ICI 4330 flat bar,ICI 4330 Valve,ICI 4330 heat exchanger parts


Related hot word search:ICI 4330 Valve ICI 4330,forging ICI 4330,ICI 4330 tube sheet,elbow ICI 4330,ICI 4330 flat bar,pipe ICI 4330,ICI 4330 Tee

Prev:ASTM 10Q
Next:ASTM 9Q