2.4608
2.4608 angle bars, 2.4608 flanges, Pipe Fitting, Steel Pipe, Heat Exchanger and Reducer, Gasket, Tee, Pipe Fitting, Tube Plate, have all specifications. With many yeas production experience, strict control 2.4608 chemical composition and 2.4608 mechanical properties.
Production specification
Data center describes many of the common steel models, we can not determine the company's warehouse has all types of steel products inventory or raw materials.
Angle bar: 1mm to 1300mm
Steel Pipe: 1 - 1300mm, also can be customed.
Pipe fitting Size: 1/8 inch - 80 inch (DN6 - DN2000)
Flange Size: DN6 - DN2000
Lenth: Any lenth based on the customer's requirement.
Steel Pipe: 1 - 1300mm, also can be customed.
Pipe fitting Size: 1/8 inch - 80 inch (DN6 - DN2000)
Flange Size: DN6 - DN2000
Lenth: Any lenth based on the customer's requirement.
|
C ≤ |
Si ≤ |
Mn ≤ |
P ≤ |
S ≤ |
Cr | Ni |
|---|---|---|---|---|---|---|
| 0.08 | 0.75-1.50 | 2.00 | 24-27 | 44-47 | ||
| Mo | Al | Cu | Nb | Ti | W | Fe |
| 2.50-4.00 | 2.50-4.00 | Balance | ||||
| N | Co | Pb | B | Other | ||
Specifications
AMS 5593, AMS 5717
ASTM B 718, ASTM B 719, ASTM B 722, ASTM B 723, ASTM B 726
UNS N06333
W. NR./EN 2.4608
Inventory
RA333® Plate, RA333® Welding Products
Common Trade Names
UNS N06333
Applications
· Tube supports in refineries and coal fired boilers
· Heat treating muffles, retorts, fan shafts and fixtures
· Carbon Fiber production muffles
· Sulfuric acid plant stack dampers
· Molten glass spinnerets
· Flare tips
· RA333 weld filler for repair welding of cast heat resistant alloys
· Tire Drop Chutes for Cement Kilns
Carburization
RA333 was originally developed to withstand high temperature carburizing service. It is one of the most carburization resistant materials available. Because of this ability RA333 has been the choice for all types of applications that require heavily carburizing atmospheres. Fabrications including radiant tubes, corrugated boxes and furnace belt pins have all been made from RA333 to withstand the high carbon potentials within these atmospheres. Resistance to metal dusting environments can be attributed to the alloying elements of silicon and tungsten. Simply having a high temperature alloy with chromium and nickel without these elements would be insufficient for a metal dusting application. Along with alloy chemistry, metal dusting resistance is influenced by grain size. A finer grain size greatly increases the rate at which chromium can diffuse to the surface to form a protective film.