A194 Gr 8M
A194 Gr 8M angle bars, A194 Gr 8M flanges, Pipe Fitting, Steel Pipe, Heat Exchanger and Reducer, Gasket, Tee, Pipe Fitting, Tube Plate, have all specifications. With many yeas production experience, strict control A194 Gr 8M chemical composition and A194 Gr 8M mechanical properties.
Production specification
Data center describes many of the common steel models, we can not determine the company's warehouse has all types of steel products inventory or raw materials.
Angle bar: 1mm to 1300mm
Steel Pipe: 1 - 1300mm, also can be customed.
Pipe fitting Size: 1/8 inch - 80 inch (DN6 - DN2000)
Flange Size: DN6 - DN2000
Lenth: Any lenth based on the customer's requirement.
Steel Pipe: 1 - 1300mm, also can be customed.
Pipe fitting Size: 1/8 inch - 80 inch (DN6 - DN2000)
Flange Size: DN6 - DN2000
Lenth: Any lenth based on the customer's requirement.
Chemical composition % of the ladle analysis of grade A194 Gr 8M and Standards
Price supply ASTM A194 / A320 Gr. 8, Gr. 8 m high pressure nut.
In the high and middle pressure valve; Sea, the ship, chemical, fluid engineering; Pressure vessels; Petrochemical equipment, and other high temperature and high pressure, low temperature high voltage equipment.
Optional exterior standard size: GB6170, GB6172, GB6175, DIN934, ANSI (UNC/UNF/UN) American standard coarse thread/fine teeth / 8 teeth permanent teeth, ANSI/ASME B18.2.2 American heavy, UNI5587 heavy, UNI5588, ASME B18.2.4.1 M, ASME B18.2.4.2 M, ASME B18.2.4.3 M, ASME B18.2.4.6 M metric hexagon nuts, etc.
Level in strict accordance with the ASTM A194 / A194M; ASME SA - 194 / SA - 194 m control.
Surface treatment: solution nature, coating teflon (PTFE), YFluo (fluorine polymer) coating, Xylan1424 coating, etc.
Machining performance
A194 Gr 8M the mechanical properties of the report, the report provides detailed performance analysis and application.
Principal Design Features
One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.
Machinability
Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.
Heat Treatment
CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.
Welding
Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.
Forging
Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.