AISI 3150
Production specification
Data center describes many of the common steel models, we can not determine the company's warehouse has all types of steel products inventory or raw materials.
Steel Pipe: 1 - 1300mm, also can be customed.
Pipe fitting Size: 1/8 inch - 80 inch (DN6 - DN2000)
Flange Size: DN6 - DN2000
Lenth: Any lenth based on the customer's requirement.
Chemical composition % of the ladle analysis of grade AISI 3150 and Standards
AISI 3150 steel (UNS G31500)
Categories: Metal; Ferrous Metal; Alloy Steel; Low Alloy Steel
Key Words: UNS G31500
Physical Properties |
Metric |
English |
Comments |
Density |
7.75 g/cc |
0.280 lb/in³ |
|
|
|||
Mechanical Properties |
Metric |
English |
Comments |
Modulus of Elasticity |
201 - 209 GPa |
29200 - 30300 ksi |
|
Bulk Modulus |
160 - 170 GPa |
23200 - 24700 ksi |
|
Poissons Ratio |
0.270 - 0.300 |
0.270 - 0.300 |
|
Shear Modulus |
81.0 - 82.0 GPa |
11700 - 11900 ksi |
|
|
|||
Thermal Properties |
Metric |
English |
Comments |
CTE, linear |
11.3 µm/m-°C |
6.28 µin/in-°F |
|
Users viewing this material also viewed the following:
AISI 3140
AISI 2330 steel (UNS G23300)
AISI 3120 steel (UNS G31200)
AISI 2515 steel (UNS G25150)
AISI 1330 steel
M3150 / 100231
Machining performance
AISI 3150 the mechanical properties of the report, the report provides detailed performance analysis and application.
Principal Design Features
One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.
Machinability
Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.
Heat Treatment
CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.
Welding
Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.
Forging
Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.
Related hot word search:AISI 3150 Valve AISI 3150,forging AISI 3150,AISI 3150 tube sheet,elbow AISI 3150,AISI 3150 flat bar,pipe AISI 3150,AISI 3150 Tee