Inconel 690 Price

Principal Design Features
A basic nickel-chromium alloy for corrosive and/or high temperature applications. The high chromium content make this alloy very resistant to attack from oxidizing chemicals or hot gases.

request for quote

Applications
High temperature burners, duct work, petrochemical heaters and furnaces. The alloy has excellent resistance to stress-corrosion cracking.

Machinability
Conventional machining techniques used for iron based alloys may be used. This alloy does work-harden during machining and has higher strength and "gumminess" not typical of steels. Heavy duty machining equipment and tooling should be used to minimize chatter or work-hardening of the alloy ahead of the cutting.

-------------------------------------------------------------------------------

Machining performance

Inconel 690 the mechanical properties of the report, the report provides detailed performance analysis and application.

--------------------------------------------------------------------------------

Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.

--------------------------------------------------------------------------------

Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.

--------------------------------------------------------------------------------

Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.

--------------------------------------------------------------------------------

Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.

--------------------------------------------------------------------------------

Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.

--------------------------------------------------------------------------------

Hot tags:Inconel 690 tube plate, Inconel 690 Pipe Fitting, Inconel 690 flange, Inconel 690 Angle Bar,Inconel 690 Valve,Inconel 690 forgings