K93600

K93600 angle bars, K93600 flanges, Pipe Fitting, Steel Pipe, Heat Exchanger and Reducer, Gasket, Tee, Pipe Fitting, Tube Plate, have all specifications. With many yeas production experience, strict control K93600 chemical composition and K93600 mechanical properties.

Production specification
Data center describes many of the common steel models, we can not determine the company's warehouse has all types of steel products inventory or raw materials.

Angle bar: 1mm to 1300mm
Steel Pipe: 1 - 1300mm, also can be customed.
Pipe fitting Size: 1/8 inch - 80 inch (DN6 - DN2000)
Flange Size: DN6 - DN2000
Lenth: Any lenth based on the customer's requirement.

Chemical composition % of the ladle analysis of grade 1.3912 and Standards

Material number 1.3912 -

Invar 36
 
 
UNS K93600
W.Nr.1.3912
X1NiCrMoCu
Fe-Ni36

K93600 Composition in % :

C

Si

Mn

P

S

Cr

Mo

Ni

max. 0,10

max. 0,50

max. 0,50

max. 0,025

max. 0,025

max. 0,50

max. 0,50

35,0 - 37,0

V

W

Ti

Cu

Al

Nb

Co

Fe

max. 1,00

60,00 - 65,00

 

K93600Machining performance

Download 1.3912 the mechanical properties of the report, the report provides detailed performance analysis and application.


K93600Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


UNS K93600Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


K93600Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


K93600Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


K93600Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.

Related hot word search:K93600 Valve K93600,forging K93600,K93600 tube sheet,elbow K93600,K93600 flat bar,pipe K93600,K93600 Tee