- Nickel 201 Valve
- Nickel 201 Flange
- Nickel 201 pipe fitting
- Nickel 201 angle bar
- Nickel 201 pipe
Nickel 201
Production specification
Data center describes many of the common steel models, we can not determine the company's warehouse has all types of steel products inventory or raw materials.
Steel Pipe: 1 - 1300mm, also can be customed.
Pipe fitting Size: 1/8 inch - 80 inch (DN6 - DN2000)
Flange Size: DN6 - DN2000
Lenth: Any lenth based on the customer's requirement.
C ≤ |
Si ≤ |
Mn ≤ |
P ≤ |
S ≤ |
Cr | Ni |
---|---|---|---|---|---|---|
0.02 | 0.15 | 0.35 | ≥99.0 | |||
Mg | Al | Cu | Nb | Ti | V | Fe |
0.15 | 0.25 | 0.1 | 0.4 | |||
N | Co | Pb | B | Other | ||
Nickel 201 Alloy Steel
Nickel 201 Alloy Steel:
Shape:tube,Steel Pipe,bar,plate,sheet,flange,Reducer,pipe fitting.
Condition:polished
Nickel 201 Alloy Steel:
Dia:1.0-400mm
Length:12M
Condition:Annealed,pickling,grinding,polishing.
Nickel 201:
UNS N02201 Din 2.4068 NA 12
Applications
1.Manufacture and handling of sodium hydroxide, particularly at temperature above 300C.
2.Production of viscose rayon. Manufacture of soap.
3.Analine hydrochloride production and in the chlorination of aliphatic hydrocarbons such as benzene, methane and ethane.
4.Manufacture of vinyl chloride monomer.
5.Reactors and vessels in which fluorine is generated and reacted with hydrocarbons.
Chemical Composition:
Ni:99.0 Min
C:≤0.02
Mn: ≤0.35
Cu: ≤0.25
S: ≤0.01
Si: ≤0.35
Fe: ≤0.40
Mechanical Properties:
Cold Worked
Ultimate Tensile Strength: 50 KSi 345 MPa Min
Yield Strength(0.2% OS): 10 KSi 70 MPa Min
Elongation:40% min
For hot-worked flats 5/16 in.(7.9mm) and under - the elongation shall be 25% min
Nickel 201 can be hot formed to almost any shape. The temperature range 1200°F to 2250°F is recommended and should be carefully abided as the proper temperature is the most important factor in achieving hot malleability. Full information of the forming process should be sought and understood before proceeding.
Nickel 201 can be cold formed by all conventional methods, but because nickel alloys have greater stiffness than stainless steels more power is required to perform the operations.
Nickel 201 is the low carbon version of Nickel 200. It is preferred to Nickel 200 for applications involving exposure to temperatures above 600°F. With low base hardness and lower work-hardening rate, it is particularly suited for cold forming.
ASTM/Din/ Specification:
Bar: ASTM B160 Din 17752 BS 3076
Sheet/Plate: ASTM B162 Din 17750 BS 3072
Fitting:B366
Forging: ASTM B564 Din 17754
Special Steel classification:
Stainless steel, Hi-Steel HSLA-80, mould steel, Heat resistant steel, Tool steel, Ball bearing steel,Spring steel, Alloy steel, Construction steel, Die steel, High-speed steel, angles, flanges, tube sheet, tee, welded pipes, seamless tubes
Standard:
Chinese GB, Japanese JIS, US ASTM, UK BS, EU DIN standards and so on.
Related hot word search:Nickel 201 Valve Nickel 201,forging Nickel 201,Nickel 201 tube sheet,elbow Nickel 201,Nickel 201 flat bar,pipe Nickel 201,Nickel 201 Tee
Prev:Nickel 200
Next:Nickel 205