- Angle bar standard
- tube standard
- pipe standard
- sheet standard
- Valve standard
- flange standard
- pipe fitting standard
ASTM A561
Production specification
Data center describes many of the common steel models, we can not determine the company's warehouse has all types of steel products inventory or raw materials.
Steel Pipe: 1 - 1300mm, also can be customed.
Pipe fitting Size: 1/8 inch - 80 inch (DN6 - DN2000)
Flange Size: DN6 - DN2000
Lenth: Any lenth based on the customer's requirement.
ASTM A561
ASTM A561
Abstract
This practice covers macroetch testing used for evaluating the quality of Tool steel bars. This test shall be used as a quality control and inspection test to reveal by deep acid etching, the macrostructure in specimens cut from bars and to show the presence, absence, and severity of the following internal, surface, or subsurface conditions: pipe, bursts, carbide or alloy segregation, nonmetallic inclusion concentrations, porosity, cracks or thermal flakes, seams, laps, ingot corner segregation, pinholes, foreign material, and ingot pattern. Macroetching may be performed in a vessel of borosilicate glass, porcelain, corrosion-resistant metals, or some other acid resisting material. The etching reagent, specimen sampling, specimen preparation, and testing procedure including etching temperature, etching time, and macroetching technique are detailed.
This abstract is a brief summary of the referenced standard. It is informational only and not an official part of the standard; the full text of the Standard itself must be referred to for its use and application. ASTM does not give any warranty express or implied or make any representation that the contents of this abstract are accurate, complete or up to date.
1. Scope
1.1 This practice for macroetch testing has been found to be a useful and reliable method for evaluating the quality of tool steel bars. It is used as a quality control and inspection test to reveal by deep acid etching the macrostructure in specimens cut from bars and to show the presence of such conditions as pipe, cracks, porosity, segregation, or foreign material. The etched surface is generally examined visually, but magnification up to about 10× is occasionally employed.
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered Standard.
Index Terms
ingot structure; macroetch; macrostructure; porosity; segregation; Macroetching; Tool steel bars;
ICS Code
ICS Number Code 77.140.60 (steel bars and rods)
DOI:10.1520/A0561-08
ASTM International is a member of CrossRef.
Related hot word search:ASTM A561 ASTM A561 Valve,ASTM A561 forging,ASTM A561 sheet,ASTM A561 coil,ASTM A561 flat bar,ASTM A561 pipe,ASTM A561 Tee
Prev:ASTM A597 - 87(2010)
Next:ASTM A700 - 05