Products are the main used in industrial manufacturing various types Ti Alloy3.7035 plate,3.7035 Valve,3.7035 forgings,3.7035 suppliers, 3.7035 Stock,3.7035 Pipe Fitting, 3.7035 Angle Bar, 3.7035 pipe,3.7035 tube,3.7035 mould,3.7035 round ingot,3.7035 cold-rolled steel,3.7035 Reducer,3.7035 strap steel,3.7035 hot-rolled steel,3.7035 medium plate, 3.7035 heavy plate,3.7035 shapped bar,3.7035 hexahedral bar,3.7035,3.7035 slab ingot,3.7035 slab,3.7035 price,3.7035 angle bar,3.7035 square steel,3.7035 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of 3.7035.
3.7035 Ti Alloy
Our advantages

3.7035 properties and heat treatment forged piece, Including 3.7035 application and specifications, Including 3.7035 tube plate, 3.7035 Pipe Fitting, 3.7035 flange, 3.7035 Angle Bar,3.7035 Valve,3.7035 3d bend.

--------------------------------------------------------------------------------

Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

--------------------------------------------------------------------------------

3.7035 has the following specifications:

Valve:
Diameter : 1mm-1300mm

Steel pipe:
Size: OD: 9.5mm - 813mm WT: 0.8mm - 34mm Length: 1 - 13m, also can be customed.

Pipe fitting:
Size: 1/8 inch - 80 inch (DN6 - DN2000) WT: Sch5s - Sch160XXS

Flange:

Length:  Any length based on the customer's requirement.

--------------------------------------------------------------------------------
Chemical composition % of the ladle analysis of grade 3.7035 and Standards

3.7035

Material No. 3.7035
EN symbol (short) Ti-II
AISI/SAE —
UNS R 50400
AFNOR —
B.S. —
Alloy —
Registered work's label Ti 994-Ti-grade2
Standards DIN 17850

Description
Our product range in 3.7025 are tubes and pipes, fittings and flanges, accessories

Chemical composition
C
≤% N
≤% H
≤% Fe
≤% O
≤% Pa
% Others
% Ti
 
0,08 0,06 0,013 0,25 0,20   0,4 rest

Special characteristics
Temperature range Density kg/dm³ Hardness HB
  approx. 4,5  
particularly good stability against corrosion, low specific weight, little cold-straining

Welding filler
Welding rod and wire electrode SG-Ti2

Main fields of application (depending on the specific conditions of use)
chemical industry, offshore platforms, aviation, space travel, highly stressed weight-saving components, condensers, sea water desalination plants, power stations

--------------------------------------------------------------------------------

Machining performance

3.7035 the mechanical properties of the report, the report provides detailed performance analysis and application.

--------------------------------------------------------------------------------

Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.

--------------------------------------------------------------------------------

Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.

--------------------------------------------------------------------------------

Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.

--------------------------------------------------------------------------------

Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.

--------------------------------------------------------------------------------

Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.

--------------------------------------------------------------------------------

Hot tags:3.7035 tube plate, 3.7035 Pipe Fitting, 3.7035 flange, 3.7035 Angle Bar,3.7035 Valve,3.7035 forgings

stainless steel | mould steel | Heat resistant steel | Tool steel | Bearing steel | Spring steel | Alloy steel | Nickel base alloy and high nickel containing steels | Cementation steels | Free-cutting steels | Cold extrusion steels | Nitriding steels | Chain steels | Carbon steel | Ti Alloy | High temperature high strength alloy and high-temperature alloy | Low alloy high-temperature steel |