99.2 Ti Ti Alloy

99.2 Ti Ti Alloy angle bars, 99.2 Ti Ti Alloy flanges, Pipe Fitting, Steel Pipe, Heat Exchanger and Reducer, Gasket, Tee, Pipe Fitting, Tube Plate, have all specifications. With many yeas production experience, strict control 99.2 Ti Ti Alloy chemical composition and 99.2 Ti Ti Alloy mechanical properties.

Production specification
Data center describes many of the common steel models, we can not determine the company's warehouse has all types of steel products inventory or raw materials.

Angle bar: 1mm to 1300mm
Steel Pipe: 1 - 1300mm, also can be customed.
Pipe fitting Size: 1/8 inch - 80 inch (DN6 - DN2000)
Flange Size: DN6 - DN2000
Lenth: Any lenth based on the customer's requirement.


Chemical composition % of the ladle analysis of grade 99.2 Ti and Standards

Category Titanium Alloy
Class Wrought
Type Commercially Pure
Designations United States: ASTM B265 Grade2, ASTM B348 Grade2, ASTM B381 Grade2, MIL-T-9046, AMS 4942, AMS 4902, AMS 4941, AMS 4951

Composition
Element Weight %
Ti  99.2

Mechanical Properties
Properties  Conditions
T (°C) Treatment
Density (×1000 kg/m3) 4.51 25  
Poisson's Ratio 0.34 25  
Elastic Modulus (GPa) 102.7 25  
Tensile Strength (Mpa) 193 315 more annealed  
Yield Strength (Mpa) 117
Elongation (%) 35 
Reduction in Area (%) 75 
Hardness (HB) 200  25 annealed 
Impact Strength (J)
(Charpy) 43 25 annealed

Thermal Properties
Properties  Conditions
T (°C) Treatment
Thermal Expansion (10-6/ºC) 8.6 20-100 more 
--------------------------------------------------------------------------------

Machining performance

99.2 Ti the mechanical properties of the report, the report provides detailed performance analysis and application.


--------------------------------------------------------------------------------

Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


--------------------------------------------------------------------------------

Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


--------------------------------------------------------------------------------

Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


--------------------------------------------------------------------------------

Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


--------------------------------------------------------------------------------

Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.