- 99.2Ti-0.2Pd Ti Alloy Valve
- 99.2Ti-0.2Pd Ti Alloy Flange
- 99.2Ti-0.2Pd Ti Alloy pipe fitting
- 99.2Ti-0.2Pd Ti Alloy angle bar
- 99.2Ti-0.2Pd Ti Alloy pipe
99.2Ti-0.2Pd Ti Alloy
Production specification
Data center describes many of the common steel models, we can not determine the company's warehouse has all types of steel products inventory or raw materials.
Steel Pipe: 1 - 1300mm, also can be customed.
Pipe fitting Size: 1/8 inch - 80 inch (DN6 - DN2000)
Flange Size: DN6 - DN2000
Lenth: Any lenth based on the customer's requirement.
99.2Ti-0.2Pd Ti Alloy
99.2Ti-0.2Pd properties and heat treatment forged piece, Including 99.2Ti-0.2Pd application and specifications, Including 99.2Ti-0.2Pd tube plate, 99.2Ti-0.2Pd Pipe Fitting, 99.2Ti-0.2Pd flange, 99.2Ti-0.2Pd Angle Bar,99.2Ti-0.2Pd Valve,99.2Ti-0.2Pd 3d bend.
99.2Ti-0.2Pd has the following specifications:
Valve:
Diameter : 1mm-1300mm
Steel pipe:
Size:
OD: 9.5mm - 813mm
WT: 0.8mm - 34mm
Length: 1 - 13m, also can be customed.
Items |
seamless pipe & tube, pipe & tube |
|||
Standard |
ASTM, GB, DIN, AISI, etc |
|||
Outer Diameter |
Round pipe9.5mm--813mm |
|||
square |
12.7x12.7--200X200mm |
|||
rectangular |
20X40--150X200mm |
|||
Thickness |
0.8mm - 34mm |
|||
Length |
5.8m,6m, or as customers' request |
|||
Tolerance |
a) Outer Diameter: +/- 0.2mm |
|||
b) Thickness: +/- 0.02mm |
||||
c) Length: +/- 5mm |
||||
Surface |
180Grit, 320Grit, 400Grit Satin / Hairline |
|||
400Grit, 500Grit, 600Grit Mirror finish |
||||
Application |
Widely used in petroleum, Foodstuff, chemical industry, construction, electric power, nuclear energy, biotechnology, machinery, papermaking, shipbuilding, boiler fields, etc |
Pipe fitting:
Size: 1/8 inch - 80 inch (DN6 - DN2000) WT: Sch5s - Sch160XXS
Items |
Elbow,Equal Tee,Reducer Tee,Concentric Reducer,Eccentric Reducer,Cap,etc |
|
Standard |
ASME |
ANSI B16.9,ANSI B16.28,MSS-SP-75 |
DIN |
DIN2605,DIN2615, DIN2616, DIN2617, DIN28011 |
|
SGP |
JISB2313 |
|
EN |
EN10253-1 EN10253-2 |
|
Material |
ASME |
A234 WPB,A234 WP1,A234 WP5,A234,WP9, A234 WPB11,A234 WPB12,A234 WPB22,WP91, A420,WPHY42,WPHY52,WPHY60,WPHY65, WPHY70,WP304,WP304L,WP304H,WP316, WP316L,WP321,WP347,WP347H |
DIN |
ST37.0,ST35.8,ST45.8,S235JR,P235GH,P265GH, 10CrMo910,15CrMo,12Cr1MoV |
|
JIS |
JIS G3454,STPG370,TPG410 |
|
Surface |
Black paint/bright paint/Galvanized |
|
Marking |
As customer’s requirements |
Flange:
Product Name | Flange | |
Items | Plate, Welding Neck, Slip on, Blind, Lap joint, Threaded Flange | |
Standard | ANSI | ANSI B16.5 ASME B16.47 series A/B |
DIN | DIN | |
GOST | GOST 12820-80 | |
EN | EN1092-1:2002 | |
JIS | JIS B2220-2004, KS D3576, KS B6216 KS B1511-2007 JIS B2261; JIS B8210 | |
BS | BS4504 BS10 Table D/E | |
Material | ANSI | CS A105/SA 105NSS 304/304L, 316/316L Alloy Steel: WHPY45/52/65/80 |
DIN | CS RST37.2;S235JR SS 304/304L,316/316L | |
GOST | CS CT20;16MN;SS 304/304L,316/316L | |
EN | CS RST37.2;S235JR;C22.8SS 304/304L,316/316L | |
JIS | SS400,SF440 SS 304/304L, 316/316L | |
BS | CSRST37.2;S235JR;C22.8;Q235SS 304/304L,316/316L | |
Pressure | ANSI | Class 150, 300, 600, 900, 1500 2500lbs |
DIN | PN6,PN10,PN16,PN25,PN40,PN64,PN100 | |
GOST | PN6,PN10,PN16,PN25 | |
EN | PN6,PN10,PN16,PN25,PN40,PN64,PN100 | |
JIS | 1K,2K,5K,10K,16K,20K,30K,40K | |
BS | PN6,PN10,PN16,PN25,PN40,PN64,PN100 | |
Size | ANSI | 1/2” – 60” |
DIN | DN15-DN2000 | |
GOST | DN15-DN1600 | |
EN | DN15-DN2000 | |
JIS | 15A-1500A | |
BS | DN15-DN2000 | |
Coating | varnish, yellow paint, anti-rust oil, galvanizing etc | |
Usage | Used for the connection of all kinds of pipeline. | |
to convey the water, steam, air, gas and oil |
Lenth: Any lenth based on the customer's requirement.
Chemical composition % of the ladle analysis of grade 99.2Ti-0.2Pd and Standards
Category Titanium Alloy
Class Wrought
Type Commercially Pure
Designations United States: ASTM B265 Grade7, ASTM B348 Grade7, ASTM B381 Grade7
Composition
Element Weight %
Ti 99.2
Pd 0.2
Mechanical Properties
Properties Conditions
T (°C) Treatment
Density (×1000 kg/m3) 4.51 25
Poisson's Ratio 0.34 25
Elastic Modulus (GPa) 102.7 25
Tensile Strength (Mpa) 186 315 more annealed
Yield Strength (Mpa) 110
Elongation (%) 37
Reduction in Area (%) 75
Hardness (HB) 200 25 annealed
Impact Strength (J)
(Charpy) 43 25 annealed
Thermal Properties
Properties Conditions
T (°C) Treatment
Thermal Expansion (10-6/ºC) 8.6 20-100 more
--------------------------------------------------------------------------------
Machining performance
99.2Ti-0.2Pd the mechanical properties of the report, the report provides detailed performance analysis and application.
--------------------------------------------------------------------------------
Principal Design Features
One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.
--------------------------------------------------------------------------------
Machinability
Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.
--------------------------------------------------------------------------------
Heat Treatment
CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.
--------------------------------------------------------------------------------
Welding
Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.
--------------------------------------------------------------------------------
Forging
Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.
stainless steel | mould steel | Heat resistant steel | Tool steel | Bearing steel | Spring steel | Alloy steel | Nickel base alloy and high nickel containing steels | Cementation steels | Free-cutting steels | Cold extrusion steels | Nitriding steels | Chain steels | Carbon steel | Ti Alloy | High temperature high strength alloy and high-temperature alloy | Low alloy high-temperature steel |
ASTMF136 h6-h9 ti alloy bar
Specifications
1.Grade: Gr5
2.Standard: ASTM F136, ISO5832-3
3. Size(mm): Dia4.76 * L(2500-3000)
4.MOQ:10KG
5.FOB:usd 50.6/kg
1.Grade: Gr5,Gr23
2.Standard: ASTM F136, ISO5832-3
3. Size(mm): Dia4.76 * L(2500-3000)
4.MOQ:10KG
5.FOB:usd 50.6/kg
6.Chemical composition:
Grade
Ti
Chemical composition
Major composition
residual elements (not more than)
Al
V
Sn
Mo
Pa
Fe
C
N
H
O
Gr5
Bal
5.5~6.75
3.5~4.5
/
/
/
0.30
0.08
0.05
0.015
0.20
Gr23
Bal
5.5~6.5
3.5~4.5
/
/
/
0.25
0.08
0.03
0.0120
0.13
7.Mechanical properties:
Material
Standard
Tensile strength (Rm/Mpa)min.
ElongationA% min.
Reduction area Z/% min.
Yield strength (Rp0.2/MPa) min.
Gr5
ASTMF136
930
10
25
860
Gr23
860
10
25
795
8.Quality Inspection:
1) Ultrasonic and eddy current testing make sure the product without cracks and scratch,
2) The infra-red detector ensure the whole bar's diameter consistency,
3) Testing Tensile strength, yield strength and so on,
4) Each product is individually inspected before dispatch.
Related hot word search:99.2Ti-0.2Pd Ti Valve 99.2Ti-0.2Pd Ti Alloy,forging 99.2Ti-0.2Pd Ti Alloy,99.2Ti-0.2Pd Ti Alloy tube sheet,elbow 99.2Ti-0.2Pd Ti Alloy,99.2Ti-0.2Pd Ti Alloy flat bar,pipe 99.2Ti-0.2Pd Ti Alloy,99.2Ti-0.2Pd Ti Alloy Tee
Prev:99.5 Ti Ti Alloy
Next:99.2 Ti Ti Alloy