Ti5Al2.5Fe Ti Alloy

Tube plate,tube Sheet,Angle Bar,Pipe tee,flange,steel pipe, pipe fitting

Site Map|Text only|XML|Contact|Payment
Home | Profile | Products | Equipment | Steel database | Quote | FAQ | Contact us | Message | Chinese |
ProductsEquipmentsSteel database   

Product category
stainless steel
mould steel
Heat resistant steel
Tool steel
Bearing steel
Spring steel
Alloy steel
Nickel base alloy and high nickel containing steels
Cementation steels
Free-cutting steels
Cold extrusion steels
Nitriding steels
Chain steels
Carbon steel
Ti Alloy
High temperature high strength alloy and high-temperature alloy
Low alloy high-temperature steel

Ti5Al2.5Fe Ti Alloy
Our advantages

Ti5Al2.5Fe properties and heat treatment forged piece, Including Ti5Al2.5Fe application and specifications, Including Ti5Al2.5Fe tube plate, Ti5Al2.5Fe Pipe Fitting, Ti5Al2.5Fe flange, Ti5Al2.5Fe Angle Bar,Ti5Al2.5Fe Valve,Ti5Al2.5Fe 3d bend.

--------------------------------------------------------------------------------

Ti5Al2.5Fe has the following specifications:

Valve:
Diameter : 1mm-1300mm

Steel pipe:
Size: OD: 9.5mm - 813mm WT: 0.8mm - 34mm Length: 1 - 13m, also can be customed.

Pipe fitting:
Size: 1/8 inch - 80 inch (DN6 - DN2000) WT: Sch5s - Sch160XXS

Flange:

Length:  Any length based on the customer's requirement.

--------------------------------------------------------------------------------
Chemical composition % of the ladle analysis of grade Ti5Al2.5Fe and Standards

Ti5Al2.5Fe ISO 5832/X
Categories:  Metal; Nonferrous Metal; Titanium Alloy; Alpha/Beta Titanium Alloy
Key Words:  medical, surgical

Physical Properties Metric English Comments
Density 4.45 g/cc 0.161 lb/in³
 
Mechanical Properties Metric English Comments
Modulus of Elasticity 110 - 116 GPa 16000 - 16800 ksi
 
Thermal Properties Metric English Comments
CTE, linear 9.30 µm/m-°C
@Temperature 30.0 - 200 °C 5.17 µin/in-°F
@Temperature 86.0 - 392 °F
Transformation Temperature 935 - 965 °C 1720 - 1770 °F
 
Component Elements Properties Metric English Comments
Aluminum, Al 4.50 - 5.50 % 4.50 - 5.50 %
Carbon, C 0.080 % 0.080 %
Hydrogen, H 0.015 % 0.015 %
Iron, Fe 2.0 - 3.0 % 2.0 - 3.0 %
Nitrogen, N 0.050 % 0.050 %
Other, each 0.10 % 0.10 %
Other, total 0.40 % 0.40 %
Oxygen, O 0.20 % 0.20 %
Titanium, Ti 90.755 - 92.755 % 90.755 - 92.755 %
 
Descriptive Properties
Microstructure Al-A9
Phase at room temp a+ß

Users viewing this material also viewed the following:
Ti6Al7Nb ASTM F1295
Overview of materials for Alpha/Beta Titanium Alloy
Overview of materials for 7000 Series Aluminum Alloy
Titanium, Ti
Ti15Mo5Zr3Al ß titanium alloy

MMEDIC24 / 12400

--------------------------------------------------------------------------------

Machining performance

Ti5Al2.5Fe the mechanical properties of the report, the report provides detailed performance analysis and application.

--------------------------------------------------------------------------------

Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.

--------------------------------------------------------------------------------

Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.

--------------------------------------------------------------------------------

Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.

--------------------------------------------------------------------------------

Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.

--------------------------------------------------------------------------------

Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.

--------------------------------------------------------------------------------

Hot tags:Ti5Al2.5Fe tube plate, Ti5Al2.5Fe Pipe Fitting, Ti5Al2.5Fe flange, Ti5Al2.5Fe Angle Bar,Ti5Al2.5Fe Valve,Ti5Al2.5Fe forgings

stainless steel | mould steel | Heat resistant steel | Tool steel | Bearing steel | Spring steel | Alloy steel | Nickel base alloy and high nickel containing steels | Cementation steels | Free-cutting steels | Cold extrusion steels | Nitriding steels | Chain steels | Carbon steel | Ti Alloy | High temperature high strength alloy and high-temperature alloy | Low alloy high-temperature steel |