Ti8Al1Mo1V Ti Alloy
Production specification
Data center describes many of the common steel models, we can not determine the company's warehouse has all types of steel products inventory or raw materials.
Steel Pipe: 1 - 1300mm, also can be customed.
Pipe fitting Size: 1/8 inch - 80 inch (DN6 - DN2000)
Flange Size: DN6 - DN2000
Lenth: Any lenth based on the customer's requirement.
Ti8Al1Mo1V Ti Alloy
Our advantages
Ti8Al1Mo1V properties and heat treatment forged piece, Including Ti8Al1Mo1V application and specifications, Including Ti8Al1Mo1V tube plate, Ti8Al1Mo1V Pipe Fitting, Ti8Al1Mo1V flange, Ti8Al1Mo1V Angle Bar,Ti8Al1Mo1V Valve,Ti8Al1Mo1V 3d bend.
--------------------------------------------------------------------------------
Introduction to Our Products:
Specialized high quality steel
We have the advantages of equipment, technologies and price
--------------------------------------------------------------------------------
Ti8Al1Mo1V has the following specifications:
Valve:
Diameter : 1mm-1300mm
Steel pipe:
Size:
OD: 9.5mm - 813mm
WT: 0.8mm - 34mm
Length: 1 - 13m, also can be customed.
Items |
seamless pipe & tube, pipe & tube |
|||
Standard |
ASTM, GB, DIN, AISI, etc |
|||
Outer Diameter |
Round pipe9.5mm--813mm |
|||
square |
12.7x12.7--200X200mm |
|||
rectangular |
20X40--150X200mm |
|||
Thickness |
0.8mm - 34mm |
|||
Length |
5.8m,6m, or as customers' request |
|||
Tolerance |
a) Outer Diameter: +/- 0.2mm |
|||
b) Thickness: +/- 0.02mm |
||||
c) Length: +/- 5mm |
||||
Surface |
180Grit, 320Grit, 400Grit Satin / Hairline |
|||
400Grit, 500Grit, 600Grit Mirror finish |
||||
Application |
Widely used in petroleum, Foodstuff, chemical industry, construction, electric power, nuclear energy, biotechnology, machinery, papermaking, shipbuilding, boiler fields, etc |
Pipe fitting:
Size: 1/8 inch - 80 inch (DN6 - DN2000) WT: Sch5s - Sch160XXS
Items |
Elbow,Equal Tee,Reducer Tee,Concentric Reducer,Eccentric Reducer,Cap,etc |
|
Standard |
ASME |
ANSI B16.9,ANSI B16.28,MSS-SP-75 |
DIN |
DIN2605,DIN2615, DIN2616, DIN2617, DIN28011 |
|
SGP |
JISB2313 |
|
EN |
EN10253-1 EN10253-2 |
|
Material |
ASME |
A234 WPB,A234 WP1,A234 WP5,A234,WP9, A234 WPB11,A234 WPB12,A234 WPB22,WP91, A420,WPHY42,WPHY52,WPHY60,WPHY65, WPHY70,WP304,WP304L,WP304H,WP316, WP316L,WP321,WP347,WP347H |
DIN |
ST37.0,ST35.8,ST45.8,S235JR,P235GH,P265GH, 10CrMo910,15CrMo,12Cr1MoV |
|
JIS |
JIS G3454,STPG370,TPG410 |
|
Surface |
Black paint/bright paint/Galvanized |
|
Marking |
As customer’s requirements |
Flange:
Product Name | Flange | |
Items | Plate, Welding Neck, Slip on, Blind, Lap joint, Threaded Flange | |
Standard | ANSI | ANSI B16.5 ASME B16.47 series A/B |
DIN | DIN | |
GOST | GOST 12820-80 | |
EN | EN1092-1:2002 | |
JIS | JIS B2220-2004, KS D3576, KS B6216 KS B1511-2007 JIS B2261; JIS B8210 | |
BS | BS4504 BS10 Table D/E | |
Material | ANSI | CS A105/SA 105NSS 304/304L, 316/316L Alloy Steel: WHPY45/52/65/80 |
DIN | CS RST37.2;S235JR SS 304/304L,316/316L | |
GOST | CS CT20;16MN;SS 304/304L,316/316L | |
EN | CS RST37.2;S235JR;C22.8SS 304/304L,316/316L | |
JIS | SS400,SF440 SS 304/304L, 316/316L | |
BS | CSRST37.2;S235JR;C22.8;Q235SS 304/304L,316/316L | |
Pressure | ANSI | Class 150, 300, 600, 900, 1500 2500lbs |
DIN | PN6,PN10,PN16,PN25,PN40,PN64,PN100 | |
GOST | PN6,PN10,PN16,PN25 | |
EN | PN6,PN10,PN16,PN25,PN40,PN64,PN100 | |
JIS | 1K,2K,5K,10K,16K,20K,30K,40K | |
BS | PN6,PN10,PN16,PN25,PN40,PN64,PN100 | |
Size | ANSI | 1/2” – 60” |
DIN | DN15-DN2000 | |
GOST | DN15-DN1600 | |
EN | DN15-DN2000 | |
JIS | 15A-1500A | |
BS | DN15-DN2000 | |
Coating | varnish, yellow paint, anti-rust oil, galvanizing etc | |
Usage | Used for the connection of all kinds of pipeline. | |
to convey the water, steam, air, gas and oil |
Length: Any length based on the customer's requirement.
--------------------------------------------------------------------------------
Chemical composition % of the ladle analysis of grade Ti8Al1Mo1V and Standards
Titanium Ti-8Al-1Mo-1V (Ti-8-1-1), Beta Annealed, Aged
Categories: Metal; Nonferrous Metal; Titanium Alloy; Alpha/Near Alpha Titanium Alloy
Material Notes: Information provided by Allvac and the references. Annealed at 1065ºC, Aged at 595ºC.
Applications: Fan & compressor blades, discs, spacers, seals, rings. Excellent creep resistance.
5 other heat treatments of this alloy are in MatWeb.
Key Words: Ti8Al1Mo1V, UNS R54810; Ti-811
Physical Properties Metric English Comments
Density 4.37 g/cc 0.158 lb/in³
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 1020 MPa 148000 psi
Tensile Strength, Yield 900 MPa 131000 psi
Elongation at Break 13.0 % 13.0 %
Modulus of Elasticity 120 GPa 17400 ksi unspecified heat treatment
Poissons Ratio 0.320 0.320 duplex annealed
Shear Modulus 46.0 GPa 6670 ksi
Electrical Properties Metric English Comments
Electrical Resistivity 0.000197 ohm-cm 0.000197 ohm-cm
Thermal Properties Metric English Comments
CTE, linear 8.50 µm/m-°C
@Temperature 20.0 °C 4.72 µin/in-°F
@Temperature 68.0 °F
9.20 µm/m-°C
@Temperature 250 °C 5.11 µin/in-°F
@Temperature 482 °F
10.1 µm/m-°C
@Temperature 500 °C 5.61 µin/in-°F
@Temperature 932 °F
Specific Heat Capacity 0.502 J/g-°C 0.120 BTU/lb-°F
Thermal Conductivity 6.00 W/m-K 41.6 BTU-in/hr-ft²-°F
Melting Point <= 1540 °C <= 2800 °F Liquidus
Liquidus 1540 °C 2800 °F
Beta Transus 1040 °C 1900 °F
Component Elements Properties Metric English Comments
Aluminum, Al 7.35 - 8.35 % 7.35 - 8.35 %
Carbon, C <= 0.0800 % <= 0.0800 %
Hydrogen, H <= 0.0150 % <= 0.0150 %
Iron, Fe <= 0.300 % <= 0.300 %
Molybdenum, Mo 0.750 - 1.25 % 0.750 - 1.25 %
Nitrogen, N <= 0.0500 % <= 0.0500 %
Other, each <= 0.100 % <= 0.100 %
Other, total <= 0.400 % <= 0.400 %
Oxygen, O <= 0.120 % <= 0.120 %
Titanium, Ti 88.185 - 91.15 % 88.185 - 91.15 % As Balance; Elemental Compostions per ASTM B265
Vanadium, V 0.750 - 1.25 % 0.750 - 1.25 %
Users viewing this material also viewed the following:
Titanium Ti-8Al-1Mo-1V (Ti-8-1-1), ST 980°C (1800°F), Aged 595°C
Titanium Ti-8Al-1Mo-1V (Ti-8-1-1)
Titanium Ti-8Al-1Mo-1V (Ti-8-1-1), Beta Solution Treated
Titanium Ti-8Al-1Mo-1V (Ti-8-1-1) Duplex Anneal
Titanium Ti-6Al-4V (Grade 5), Annealed
MTA811 / 14136
--------------------------------------------------------------------------------
Machining performance
Ti8Al1Mo1V the mechanical properties of the report, the report provides detailed performance analysis and application.
--------------------------------------------------------------------------------
Principal Design Features
One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.
--------------------------------------------------------------------------------
Machinability
Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.
--------------------------------------------------------------------------------
Heat Treatment
CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.
--------------------------------------------------------------------------------
Welding
Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.
--------------------------------------------------------------------------------
Forging
Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.
--------------------------------------------------------------------------------
stainless steel | mould steel | Heat resistant steel | Tool steel | Bearing steel | Spring steel | Alloy steel | Nickel base alloy and high nickel containing steels | Cementation steels | Free-cutting steels | Cold extrusion steels | Nitriding steels | Chain steels | Carbon steel | Ti Alloy | High temperature high strength alloy and high-temperature alloy | Low alloy high-temperature steel |
Related hot word search:Ti8Al1Mo1V Ti Valve Ti8Al1Mo1V Ti Alloy,forging Ti8Al1Mo1V Ti Alloy,Ti8Al1Mo1V Ti Alloy tube sheet,elbow Ti8Al1Mo1V Ti Alloy,Ti8Al1Mo1V Ti Alloy flat bar,pipe Ti8Al1Mo1V Ti Alloy,Ti8Al1Mo1V Ti Alloy Tee
Prev:Ti-811 Ti Alloy
Next:UNS R54810 Ti Alloy