Titanium 1100 Ti Alloy
Production specification
Data center describes many of the common steel models, we can not determine the company's warehouse has all types of steel products inventory or raw materials.
Steel Pipe: 1 - 1300mm, also can be customed.
Pipe fitting Size: 1/8 inch - 80 inch (DN6 - DN2000)
Flange Size: DN6 - DN2000
Lenth: Any lenth based on the customer's requirement.
Titanium 1100 Ti Alloy
Our advantages
Titanium 1100 properties and heat treatment forged piece, Including Titanium 1100 application and specifications, Including Titanium 1100 tube plate, Titanium 1100 Pipe Fitting, Titanium 1100 flange, Titanium 1100 Angle Bar,Titanium 1100 Valve,Titanium 1100 3d bend.
--------------------------------------------------------------------------------
Introduction to Our Products:
Specialized high quality steel
We have the advantages of equipment, technologies and price
--------------------------------------------------------------------------------
Titanium 1100 has the following specifications:
Valve:
Diameter : 1mm-1300mm
Steel pipe:
Size:
OD: 9.5mm - 813mm
WT: 0.8mm - 34mm
Length: 1 - 13m, also can be customed.
Items |
seamless pipe & tube, pipe & tube |
|||
Standard |
ASTM, GB, DIN, AISI, etc |
|||
Outer Diameter |
Round pipe9.5mm--813mm |
|||
square |
12.7x12.7--200X200mm |
|||
rectangular |
20X40--150X200mm |
|||
Thickness |
0.8mm - 34mm |
|||
Length |
5.8m,6m, or as customers' request |
|||
Tolerance |
a) Outer Diameter: +/- 0.2mm |
|||
b) Thickness: +/- 0.02mm |
||||
c) Length: +/- 5mm |
||||
Surface |
180Grit, 320Grit, 400Grit Satin / Hairline |
|||
400Grit, 500Grit, 600Grit Mirror finish |
||||
Application |
Widely used in petroleum, Foodstuff, chemical industry, construction, electric power, nuclear energy, biotechnology, machinery, papermaking, shipbuilding, boiler fields, etc |
Pipe fitting:
Size: 1/8 inch - 80 inch (DN6 - DN2000) WT: Sch5s - Sch160XXS
Items |
Elbow,Equal Tee,Reducer Tee,Concentric Reducer,Eccentric Reducer,Cap,etc |
|
Standard |
ASME |
ANSI B16.9,ANSI B16.28,MSS-SP-75 |
DIN |
DIN2605,DIN2615, DIN2616, DIN2617, DIN28011 |
|
SGP |
JISB2313 |
|
EN |
EN10253-1 EN10253-2 |
|
Material |
ASME |
A234 WPB,A234 WP1,A234 WP5,A234,WP9, A234 WPB11,A234 WPB12,A234 WPB22,WP91, A420,WPHY42,WPHY52,WPHY60,WPHY65, WPHY70,WP304,WP304L,WP304H,WP316, WP316L,WP321,WP347,WP347H |
DIN |
ST37.0,ST35.8,ST45.8,S235JR,P235GH,P265GH, 10CrMo910,15CrMo,12Cr1MoV |
|
JIS |
JIS G3454,STPG370,TPG410 |
|
Surface |
Black paint/bright paint/Galvanized |
|
Marking |
As customer’s requirements |
Flange:
Product Name | Flange | |
Items | Plate, Welding Neck, Slip on, Blind, Lap joint, Threaded Flange | |
Standard | ANSI | ANSI B16.5 ASME B16.47 series A/B |
DIN | DIN | |
GOST | GOST 12820-80 | |
EN | EN1092-1:2002 | |
JIS | JIS B2220-2004, KS D3576, KS B6216 KS B1511-2007 JIS B2261; JIS B8210 | |
BS | BS4504 BS10 Table D/E | |
Material | ANSI | CS A105/SA 105NSS 304/304L, 316/316L Alloy Steel: WHPY45/52/65/80 |
DIN | CS RST37.2;S235JR SS 304/304L,316/316L | |
GOST | CS CT20;16MN;SS 304/304L,316/316L | |
EN | CS RST37.2;S235JR;C22.8SS 304/304L,316/316L | |
JIS | SS400,SF440 SS 304/304L, 316/316L | |
BS | CSRST37.2;S235JR;C22.8;Q235SS 304/304L,316/316L | |
Pressure | ANSI | Class 150, 300, 600, 900, 1500 2500lbs |
DIN | PN6,PN10,PN16,PN25,PN40,PN64,PN100 | |
GOST | PN6,PN10,PN16,PN25 | |
EN | PN6,PN10,PN16,PN25,PN40,PN64,PN100 | |
JIS | 1K,2K,5K,10K,16K,20K,30K,40K | |
BS | PN6,PN10,PN16,PN25,PN40,PN64,PN100 | |
Size | ANSI | 1/2” – 60” |
DIN | DN15-DN2000 | |
GOST | DN15-DN1600 | |
EN | DN15-DN2000 | |
JIS | 15A-1500A | |
BS | DN15-DN2000 | |
Coating | varnish, yellow paint, anti-rust oil, galvanizing etc | |
Usage | Used for the connection of all kinds of pipeline. | |
to convey the water, steam, air, gas and oil |
Length: Any length based on the customer's requirement.
--------------------------------------------------------------------------------
Chemical composition % of the ladle analysis of grade Titanium 1100 and Standards
Titanium 1100 Beta Quenched and annealed
Categories: Metal; Nonferrous Metal; Titanium Alloy; Alpha/Near Alpha Titanium Alloy
Material Notes:
Key Words: Titanium 1100
Physical Properties Metric English Comments
Density 4.50 g/cc 0.163 lb/in³
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 1010 MPa 146000 psi
750 MPa
@Temperature 400 °C 109000 psi
@Temperature 752 °F
Tensile Strength, Yield 910 MPa 132000 psi
625 MPa
@Temperature 400 °C 90600 psi
@Temperature 752 °F
Elongation at Break 11.0 % 11.0 %
Modulus of Elasticity 107 - 117 GPa 15500 - 17000 ksi
Poissons Ratio 0.310 0.310 Typical for alpha titanium alloy.
Fatigue Strength 250 MPa
@# of Cycles 1.00e+7 36300 psi
@# of Cycles 1.00e+7 notched with Kt = 3.0.
655 MPa
@# of Cycles 1.00e+7 95000 psi
@# of Cycles 1.00e+7 notched with Kt = 1.0.
Fracture Toughness 63.0 MPa-m½ 57.3 ksi-in½ K(IC) after 1095ºC anneal
Shear Modulus 42.7 GPa 6190 ksi Calculated from typical values.
Electrical Properties Metric English Comments
Electrical Resistivity 0.000160 ohm-cm 0.000160 ohm-cm Estimated from similar alpha titanium alloys.
Thermal Properties Metric English Comments
CTE, linear 9.00 µm/m-°C
@Temperature 20.0 - 100 °C 5.00 µin/in-°F
@Temperature 68.0 - 212 °F Typical alpha titanium alloy
Specific Heat Capacity 0.525 J/g-°C 0.125 BTU/lb-°F Typical value for titanium alloys.
Thermal Conductivity 7.00 W/m-K 48.6 BTU-in/hr-ft²-°F Estimated from similar titanium alloys.
Beta Transus 1015 °C 1859 °F
Component Elements Properties Metric English Comments
Aluminum, Al 6.0 % 6.0 %
Molybdenum, Mo 0.40 % 0.40 %
Silicon, Si 0.40 % 0.40 %
Tin, Sn 2.70 % 2.70 %
Titanium, Ti 87.0 % 87.0 %
Zirconium, Zr 4.0 % 4.0 %
Users viewing this material also viewed the following:
Aluminum 6061-T6; 6061-T651
AISI 4140 Steel, normalized at 870°C (1600°F), air cooled, 100 mm (4 in.) round
Titanium, Ti
Allegheny Ludlum Grade 1 Titanium (UNS R50250)
Titanium Ti-3Al-2.5V (Grade 9), alpha annealed
MTA993 / 14143
--------------------------------------------------------------------------------
Machining performance
Titanium 1100 the mechanical properties of the report, the report provides detailed performance analysis and application.
--------------------------------------------------------------------------------
Principal Design Features
One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.
--------------------------------------------------------------------------------
Machinability
Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.
--------------------------------------------------------------------------------
Heat Treatment
CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.
--------------------------------------------------------------------------------
Welding
Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.
--------------------------------------------------------------------------------
Forging
Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.
--------------------------------------------------------------------------------
Hot tags:Titanium 1100 tube plate, Titanium 1100 Pipe Fitting, Titanium 1100 flange, Titanium 1100 Angle Bar,Titanium 1100 Valve,Titanium 1100 forgings
stainless steel | mould steel | Heat resistant steel | Tool steel | Bearing steel | Spring steel | Alloy steel | Nickel base alloy and high nickel containing steels | Cementation steels | Free-cutting steels | Cold extrusion steels | Nitriding steels | Chain steels | Carbon steel | Ti Alloy | High temperature high strength alloy and high-temperature alloy | Low alloy high-temperature steel |
Related hot word search:Titanium 1100 Valve Titanium 1100 Ti Alloy,forging Titanium 1100 Ti Alloy,Titanium 1100 Ti Alloy tube sheet,elbow Titanium 1100 Ti Alloy,Titanium 1100 Ti Alloy flat bar,pipe Titanium 1100 Ti Alloy,Titanium 1100 Ti Alloy Tee
Prev:Ti 10-2-3 Ti Alloy
Next:IMI 834 Ti Alloy