UNS R54810 Ti Alloy

UNS R54810 Ti Alloy
Our advantages

UNS R54810 properties and heat treatment forged piece, Including UNS R54810 application and specifications, Including UNS R54810 tube plate, UNS R54810 Pipe Fitting, UNS R54810 flange, UNS R54810 Angle Bar,UNS R54810 Valve,UNS R54810 3d bend.

--------------------------------------------------------------------------------

Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

--------------------------------------------------------------------------------

UNS R54810 has the following specifications:

Valve:
Diameter : 1mm-1300mm

Steel pipe:
Size: OD: 9.5mm - 813mm WT: 0.8mm - 34mm Length: 1 - 13m, also can be customed.

Pipe fitting:
Size: 1/8 inch - 80 inch (DN6 - DN2000) WT: Sch5s - Sch160XXS

Flange:

Length:  Any length based on the customer's requirement.

--------------------------------------------------------------------------------
Chemical composition % of the ladle analysis of grade UNS R54810 and Standards

Titanium Ti-8Al-1Mo-1V (Ti-8-1-1), Beta Annealed, Aged
Categories: Metal; Nonferrous Metal; Titanium Alloy; Alpha/Near Alpha Titanium Alloy

Material Notes: Information provided by Allvac and the references. Annealed at 1065ºC, Aged at 595ºC.

Applications: Fan & compressor blades, discs, spacers, seals, rings. Excellent creep resistance.

5 other heat treatments of this alloy are in MatWeb.

Key Words: Ti8Al1Mo1V, UNS R54810; Ti-811

Physical Properties Metric English Comments
Density 4.37 g/cc 0.158 lb/in³
 
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 1020 MPa 148000 psi
Tensile Strength, Yield 900 MPa 131000 psi
Elongation at Break 13.0 % 13.0 %
Modulus of Elasticity 120 GPa 17400 ksi unspecified heat treatment
Poissons Ratio 0.320 0.320 duplex annealed
Shear Modulus 46.0 GPa 6670 ksi
 
Electrical Properties Metric English Comments
Electrical Resistivity 0.000197 ohm-cm 0.000197 ohm-cm
 
Thermal Properties Metric English Comments
CTE, linear 8.50 µm/m-°C
@Temperature 20.0 °C 4.72 µin/in-°F
@Temperature 68.0 °F
  9.20 µm/m-°C
@Temperature 250 °C 5.11 µin/in-°F
@Temperature 482 °F
  10.1 µm/m-°C
@Temperature 500 °C 5.61 µin/in-°F
@Temperature 932 °F
Specific Heat Capacity 0.502 J/g-°C 0.120 BTU/lb-°F
Thermal Conductivity 6.00 W/m-K 41.6 BTU-in/hr-ft²-°F
Melting Point <= 1540 °C <= 2800 °F Liquidus
Liquidus 1540 °C 2800 °F
Beta Transus 1040 °C 1900 °F
 
Component Elements Properties Metric English Comments
Aluminum, Al 7.35 - 8.35 % 7.35 - 8.35 %
Carbon, C <= 0.0800 % <= 0.0800 %
Hydrogen, H <= 0.0150 % <= 0.0150 %
Iron, Fe <= 0.300 % <= 0.300 %
Molybdenum, Mo 0.750 - 1.25 % 0.750 - 1.25 %
Nitrogen, N <= 0.0500 % <= 0.0500 %
Other, each <= 0.100 % <= 0.100 %
Other, total <= 0.400 % <= 0.400 %
Oxygen, O <= 0.120 % <= 0.120 %
Titanium, Ti 88.185 - 91.15 % 88.185 - 91.15 % As Balance; Elemental Compostions per ASTM B265
Vanadium, V 0.750 - 1.25 % 0.750 - 1.25 %

Users viewing this material also viewed the following:
Titanium Ti-8Al-1Mo-1V (Ti-8-1-1), ST 980°C (1800°F), Aged 595°C
Titanium Ti-8Al-1Mo-1V (Ti-8-1-1)
Titanium Ti-8Al-1Mo-1V (Ti-8-1-1), Beta Solution Treated
Titanium Ti-8Al-1Mo-1V (Ti-8-1-1) Duplex Anneal
Titanium Ti-6Al-4V (Grade 5), Annealed

MTA811 / 14136

--------------------------------------------------------------------------------

Machining performance

UNS R54810 the mechanical properties of the report, the report provides detailed performance analysis and application.

--------------------------------------------------------------------------------

Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.

--------------------------------------------------------------------------------

Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.

--------------------------------------------------------------------------------

Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.

--------------------------------------------------------------------------------

Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.

--------------------------------------------------------------------------------

Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.

--------------------------------------------------------------------------------

Hot tags:UNS R54810 tube plate, UNS R54810 Pipe Fitting, UNS R54810 flange, UNS R54810 Angle Bar,UNS R54810 Valve,UNS R54810 forgings

stainless steel | mould steel | Heat resistant steel | Tool steel | Bearing steel | Spring steel | Alloy steel | Nickel base alloy and high nickel containing steels | Cementation steels | Free-cutting steels | Cold extrusion steels | Nitriding steels | Chain steels | Carbon steel | Ti Alloy | High temperature high strength alloy and high-temperature alloy | Low alloy high-temperature steel |