SPECIFICATIONS: GRADE Duplex | UNS S31803 | ASTM/ASME A240 / F51 | Werkstoff 1.4462

Zhejiang Yaang Pipe Industry Co., Limited is a professional organizer and one-stop-shop supplier for special steel, duplex steel, duplex stainless steel flangessuper duplex stainless steel flangesstainless steel flangesStainless Steel Pipesstainless steel pipe fittings etc.


The following are the properties of 31803:

  • Stainless ferritic-austenitic Cr-Ni-Mo steel with nitrogen addition.
  • High corrosion resistance, especially against stress corrosion cracking in solutions containing chloride.
  • Good strength properties.
  • Resistant to intergranular corrosion in the temperature range up to 300°C.
  • Heat treatment subsequent to welding not necessary.
  • Surface condition for optimum corrosion resistance: pickled, heat treated free from scale or machined.

Application

Components in the chemical industry, e.g. separator and heat exchanger parts, from the paper industry, oil and gas production, compressor parts, seawater desalination plants.

Chemical Composition (average %)

C Si Mn Cr Mo Ni N
0.025 0.60 1.30 22.60 3.20 5.80 0.17

Standards

EN / DIN ASTM UNS AFNOR
<1.4462 >
X2CrNiMoN22-5-3
A240 S31803 Z2CND22-5 Az

Hot Forming

Forging

1200 to 950°C / Air cooling

Heat Treatment

Solution annealing:

1020 to 1100°C
Water , air (thickness below 2mm)

Structure

Ferrite + Austenite

Condition: solution annealed

Product Dimension
Size
mm
0.2% proof stress
N/mm2
min.
Tensile strength
N/mm2
Elongation A5
% min.
L    Q     T
Impact strength
(ISO-V)
J min.
L    Q     T
St ≤ 160 450 650 – 880 25   - –    - - 100   - –    - -
Bl ≤ 75 460 640 – 840 252)  252)  - - 90   60    - -

St = Bar ,
Bl = Sheet or plate
L = Longitudinal, Q = Transverse, T = Tangential
1) For sheet or plate < 3mm = A80mm specimen
The values for other products and dimensions shall be established by
agreement.

Condition: solution annealed

0.2% proof stress
N/mm2
min.
Temperature
100°C 150°C 200°C 250°C
360 335 315 300

Welding

Good weldability. Welding is possible with all processes usual for stainless steels. We recommend depending on applications electric arc welding with covered electrodes, inert gas welding or SA-welding. Preheating and heat treatment after welding is not necessary. For high stressed heavy walled constructions the limited preheat temperature of 150°C maximum is recommendable. Maximum interpass temperature 150°C. Keep heat input low especially for small wall thicknesses. The TIG-process should be given reference for root welding.

Thermal conductivity at ……………….. 20°C ………………15.0 ………W/(m.K)
Specific heat at …………………………..20°C ………………500 ……….J/(kg.K)
Electrical resistivity at …………………. 20°C ………………0.80 ………Ohm.mm2/m
Modulus of elasticity at ……………….. 20°C ………………200 x 103 N/mm2
Magnetic properties ……………………………………………..magnetic

Thermal expansion between
20°C and …°C, 10-6 m/(m.K) at
Temperature 10-6 m/(m.K)
100°C 13.0
200°C 13.5
300°C 14.0
Modulus of elasticity, 103 N/mm2 at Temperature 103 N/mm2
20°C 200
100°C 194
200°C 186
300°C 180

As regards applications and processing steps that are not expressly mentioned in this product description/data sheet, the customer shall in each individual case be required to consult us.

Tel No:+86-18267732328 / Fax No :86-0577-56809281 / Email:sales@yaang.com
Address:Longwan District, Wenzhou, Zhejiang Province, China.

Copyright Notice © Yaang.com Yaang Pipe Industry Co., Limited All rights reserved.
Yaang Pipe Industry Co., Ltd. is an international supplier of piping solutions for flange, butt welding fittings, socket welding fittings and threaded fittings. Our products are widely used in different industrial fields, including oil and gas, chemical industry, petrochemical industry, power plant, pulp and paper industry, environmental and water conservancy engineering, engineering projects, etc.