Ξ
- SITEMAP
- CONTACT US
- 8618267732328
News
Credibility ,the lifeblood of enterprise!
PRODUCT SERIES
- Fittings
- Butt Welding Fittings
- Forged Fittings
- 180 Degree Elbows
- 90 Degree Elbows
- 60 Degree Elbows
- 45 Degree Elbows
- 30 Degree Elbows
- Equal Tee
- Reducing Tee
- Concentric Reducer
- Eccentric Reducer
- Lap Joint Stub End
- Outlets
- Cap
- Bend
- Cross
- Coupling
- Stainless Steel Lateral Tee
- Bellows Expansion Joints
- Flexible Metal Hose
- Non-Standard/Custom Fittings
- Bleed & Flushing Rings
- Types of Flanges
- Anchor Flanges
- Blind Flanges
- Expander Flanges
- High Hub Flanges
- Lap Joint Flanges
- Long Weld Neck Flanges
- Nipoflanges
- Orifice Flanges
- Plate Flanges
- Ring Type Joint Flanges
- Reducing Flanges
- Slip On Flanges
- Socket Weld Flanges
- Spectacle Blind Flanges
- Square Flanges
- Spades & Ring Spacers
- Threaded Flanges
- Welding Neck Flanges
Your Location: Home > News
News - Yaang
Several processes of pickling and passivation on the surface of stainless steel plate
DataTime:[2018-11-8]
When the surface of the stainless steel plate is not annealed (for example, the surface after welding), drilling mud residue, rust-proof film, or ferrite impregnated with stainless steel after the molding process, the corrosion resistance of the stainless steel material will be directly affected. At this point you need to use acidic oil cleaning agent to do the appropriate cleaning and maintenance operations on the stainless steel surface.
Stainless steel pickling passivation can completely remove impurities and promote the formation of a new passivation layer, which is a complete chemical reaction process. It can not only clean the surface of the stainless steel plate, but also can form a completely uniform silver white on the surface of the treated stainless steel plate. According to actual tasks, stainless steel plates with different structures and surface sizes can use different pickling products.
First look at the stainless steel pickling passivation paste, this product is used to deal with the surface of the larger stainless steel plate or surface weld around the weld spot, oxide layer color, as long as the uniform smear on the surface of the stainless steel plate, wait until The surface of the stainless steel plate is completely uniform and white.
Followed by the stainless steel pickling passivation solution, which is mainly used for the pickling of small serial parts, such products are easy to immerse, usually using plastic containers soaked at room temperature, and even can achieve high efficiency pickling and passivation done synchronously, such as stainless steel After the surface of the board has been pickled and passivated, the maximum salt spray resistance can reach about 500 hours.
In addition to the pickling spray, this process is suitable for pickling large stainless steel surfaces (including wall panels, containers) as well as non-removable structures or difficult-to-access structures such as bridge components. Pickling sprays can increase application control.
There is also ablation pickling. This technique can remove the surface tension and internal stress of the stainless steel plate material by specifically removing the 3-5 micron surface, and also remove surface microcracking.
However, no matter which process is used, the treated surface acid must be completely cleaned. It is best to use high-pressure cleaning.
Source: China Stainless Steel Plates Manufacturer - Yaang Pipe Industry Co., Limited (www.yaang.com)
Stainless steel pickling passivation can completely remove impurities and promote the formation of a new passivation layer, which is a complete chemical reaction process. It can not only clean the surface of the stainless steel plate, but also can form a completely uniform silver white on the surface of the treated stainless steel plate. According to actual tasks, stainless steel plates with different structures and surface sizes can use different pickling products.
First look at the stainless steel pickling passivation paste, this product is used to deal with the surface of the larger stainless steel plate or surface weld around the weld spot, oxide layer color, as long as the uniform smear on the surface of the stainless steel plate, wait until The surface of the stainless steel plate is completely uniform and white.
Followed by the stainless steel pickling passivation solution, which is mainly used for the pickling of small serial parts, such products are easy to immerse, usually using plastic containers soaked at room temperature, and even can achieve high efficiency pickling and passivation done synchronously, such as stainless steel After the surface of the board has been pickled and passivated, the maximum salt spray resistance can reach about 500 hours.
In addition to the pickling spray, this process is suitable for pickling large stainless steel surfaces (including wall panels, containers) as well as non-removable structures or difficult-to-access structures such as bridge components. Pickling sprays can increase application control.
There is also ablation pickling. This technique can remove the surface tension and internal stress of the stainless steel plate material by specifically removing the 3-5 micron surface, and also remove surface microcracking.
However, no matter which process is used, the treated surface acid must be completely cleaned. It is best to use high-pressure cleaning.
Source: China Stainless Steel Plates Manufacturer - Yaang Pipe Industry Co., Limited (www.yaang.com)
Tel No：+86-18267732328 / Email:[email protected]
Address：Longwan District, Wenzhou, Zhejiang Province, China.
Copyright Notice © www.yaang.com Yaang Pipe Industry Co., Limited All rights reserved.
Yaang Pipe Industry Co., Ltd. is an international supplier of piping solutions for flange, butt welding fittings, socket welding fittings and threaded fittings. Our products are widely used in different industrial fields, including oil and gas, chemical industry, petrochemical industry, power plant, pulp and paper industry, environmental and water conservancy engineering, engineering projects, etc.