ISO 50CrMoV13-15

ISO 50CrMoV13-15 angle bars, ISO 50CrMoV13-15 flanges, Pipe Fitting, Steel Pipe, Heat Exchanger and Reducer, Gasket, Tee, Pipe Fitting, Tube Plate, have all specifications. With many yeas production experience, strict control ISO 50CrMoV13-15 chemical composition and ISO 50CrMoV13-15 mechanical properties.

Production specification
Data center describes many of the common steel models, we can not determine the company's warehouse has all types of steel products inventory or raw materials.

Angle bar: 1mm to 1300mm
Steel Pipe: 1 - 1300mm, also can be customed.
Pipe fitting Size: 1/8 inch - 80 inch (DN6 - DN2000)
Flange Size: DN6 - DN2000
Lenth: Any lenth based on the customer's requirement.

ISO 50CrMoV13-15

ISO 50CrMoV13-15 tube plate, ISO 50CrMoV13-15 flange, ISO 50CrMoV13-15 steel Pipe Fitting, ISO 50CrMoV13-15 Reducer, ISO 50CrMoV13-15 angle bar, ISO 50CrMoV13-15 Valve, ISO 50CrMoV13-15 steel pipe, ISO 50CrMoV13-15 tube, ISO 50CrMoV13-15 tube sheet, ISO 50CrMoV13-15 tee. ISO 50CrMoV13-15 chemical composition and mechanical properties.
 
Specific feature is as follows:

Chemical composition - Hot working alloy tool steel
Steel grade: ISO 50CrMoV13-15
 
C(%):    0.45~0.55
Si(%):    0.20~0.80
Mn(%):    0.50~0.90
P(%)≤:    0.030
S(%)≤:    0.020
Cr(%):    3.00~3.50
Mo(%):    1.30~1.70
V(%):    0.15~0.35
W(%):    —
Other(%):    —
Hardness and heat treatment
Hardness after annealing ≤HBW:  248
Quenching |quenching temperature /(℃±10℃):  1010
Quenching medium : oil
Tempering temperature /(℃±10℃):   510
Hardness after tempering ≥HRC:56

Main feature and application field – alloy tool steel
 
Alloy tool steel
 is widely used to produce the cutting tool, cold/heat distortion mould and measuring implement. and further to manufacture the piston, valve, valve seat of fuel pump of diesel engine.
 
Object classification
 
The hardening capacity, hardenability, abrasive resistance and toughness of alloy tool steel are superior to carbon tool steel,it roughly divides into cutting toolmould steel, measuring implement steel according to its application. The high-carbon content steel (carbon mass fraction is over 0.080% ) is used to process the cutting tool, measuring implement and cold work die. the hardness is over HRC60 after quenching. and has enough abrasive resistance. The steel of medium carbon content (mass fraction 0.35%~ 070%) is generally used to make the hot working die, low speed cutting tools ( woodworking tool, benchwork tool, drill, milling cutter) and measuring implements (caliper, micrometer, block gauge, sample plale). Measuring and cutting tool steel should have high hardness (62~65HRC),high abrasive resistance, enough obdurability, hothardness. The measuring and cutting tool steel also should require excellent dimensional stability in order for a higher precision.
 
Cold work die includes cold punching mould, wire-drawing die, drawing die, coining die, thread rolling die, cold heading die, cold extrusion die, Based on the working condition, cold work die should have the high hardness, strength, abrasion resistance, toughness, hardenability, quenching degree, and other processing property. This kind of alloy tool steel belongs to  high carbon Alloy steel (carbon mass fraction is over 0.80%), Chromium is key element of alloy with mass fraction below 5% generally.
 
Hot-working die divides into several main types, such as hammer flanges, die flanges, extrusion and die casting, including hot forging diepress machine forging die, stamping die, hot-extrusion die, metal die-casting mould. Heat distortion mould not only supports huge mechanical stress, but also thermal stress during working repeatedly. Hot-work die steel should have not only high hardness, red hardness, abrasion resistance, toughness, but also have excellent high temperature strength, thermal fatigue stability, thermal conductivity, upper hardenability for guaranteeing the whole cross section with consistent mechanical property
 
Plastic mold includes thermoplastic plastic mould and thermosetting plastic mold. Plastic mould steel requires the properties of definite strength, hardness, abrasion resistance, heat stability and corrosion resistance. And further requires excellent manufacturability, such as processability, corrosion resistance, grindability, polishing, repair welding, roughness, thermal conductivity, shape stability.
Heat treatment
 
The preheating of measuring and cutting tool steel is spheroidizing annealing, final heat treatment is quenching + low temperature tempering and hardness after heat treatment can reach 60~65HRC.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering
    any other conditions based on the customer's requirement
Surface conditions: flaking /turning /grinding /polishing /buffing /acid /rough machining /fine machining
  any other processing technics based on the customer's special requirements.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirement.
   Excellent service for all kinds of industries with advantages of technologies, equipments and affordable price.

Related hot word search:ISO 50CrMoV13-15 Valve ISO 50CrMoV13-15,forging ISO 50CrMoV13-15,ISO 50CrMoV13-15 tube sheet,elbow ISO 50CrMoV13-15,ISO 50CrMoV13-15 flat bar,pipe ISO 50CrMoV13-15,ISO 50CrMoV13-15 Tee

Prev:ISO X40CrMoV5-1
Next:ISO X30WCrV9-3