Stainless Steel 410

Stainless steel 410 is a basic martensitic grade which contains 11.5% chromium, offering both exceptional wear and corrosion resistance. Stainless steel 410 is corrosion resistant to some chemicals, food, mild acids, water, and air. It also proves adequate resistance to nitric acid, concentrated sulfuric acid, dilute acetic acid and naphtha. Elevated mechanical properties and corrosion resistance are achieved with stainless steel 410 when it's hardened and tempered. 

Stainless steel 410 is used in applications such as dental and surgical instruments, pipelines, valves and nozzles, automotive parts and more.Stainless steel 410 is generally used for applications which involve mild corrosion, high strength, and heat resistance.  Please contact Yaang Pipe Industry for more information about stainless steel 410, its properties, and its applications.

Heat Treatment:

Galvanizing: Heat slowly to 1500 -1650°F, cool to 1100°F in furnace, air cool. Process Galvanizing: Heat to 1350 -1450°F, air cool. Hardening: Heat to 1700 - 1850°F, air cool or oil quench. Follow by temper or stress-relief. Stress Relieving: Heat at 300 - 800°F for 1 to 2 hours, air cool. See our stainless steel heat treating services.

Forming:

Stainless steel 410 has cold working properties which allow it to be temperately drawn and shaped in the galvanized condition.

Fabrication:

The martensitic alloys offer unique hardening capabilities which limit their capability of being welded using conventional techniques. Stainless steel 410must first be pre-heated, followed by a post-weld galvanizing treatment to alleviate cracking.

Stainless Steel 410 Flanges Stock

• Blind Flanges
• Lap Joint Flanges
• Weld Neck Flanges
• Slip On Flanges
  
• Plate Flanges

Stainless Steel 410 Pipes Stock

• Welded Steel Pipes
• Seamless Steel Pipes
• Heat Exchanger Tubes
• ERW Pipes
  
• Cold Draw Seamless Pipes

Stainless Steel 410 Pipe Fittings Stock

• Butt Welding Fittings
• Forged Fittingss
• Equal Tee
• Reducing Tee
  
• Concentric Reducer

Stainless Steel 410 Mechanical Properties

Material Type	Condition	Ultimate Tensile Strength (PSI)	0.2% Yield Strength (PSI)	Elongation (% In 2in.)	Reduction Of Area (%)	Hardness Brinell	Hardness Rockwell
Stainless steel 410	T	100,000	80,000	12	40	*	*
	H	120,000	90,000	12	40	*	*
	Annealed	70,000	40,000	16	45	*	*
	Class2	110,000	85,000	15	45	269 Max	*
	NACE MRO 175	*	*	*	*	*	22 HRC Max

Our website: www.yaang.com . Please send your detailed requirements to [email protected]. We will give you the best offer.