Stainless Steel 317L Material Property Data

DataTime:[2014-11-13]

Stainless Steel 317L (UNS S31703) is a molybdenum-bearing austenitic stainless steel with greatly increased resistance to chemical attack as compared to the conventional chromium-nickel austenitic stainless steel pipe such as SS 304 and SS 316L.

Specifications

The following specifications cover Stainless Steel 317L

  • AISI 317L
  • ASTM A167
  • ASTM A182
  • ASTM A213
  • ASTM A240
  • ASTM A249
  • ASTM A312
  • ASTM A774
  • ASTM A778
  • ASTM A813
  • ASTM A814
  • DIN 1.4438
  • QQ S763
  • UNS S31703

Related Metals:

  • 3R64(tm)
  • AF 317L(tm)
Chemistry Data :

Carbon

0.03 max

Chromium

18 - 20

Iron

Balance

Manganese

2 max

Molybdenum

3 - 4

Nickel

11 - 15

Phosphorus

0.045 max

Silicon

1 max

Sulphur

0.03 max

Forms

Stainless Steel Flanges - Slip on flanges, Blind flanges, Lap joint flanges, Welding neck flanges, Spectacle flanges, TG flanges, Socket welding flanges and Threaded flanges, Square flanges.
Stainless Steel Pipe Fittings - Butt Welding Fittings, Forged Fittings, 180 Degree Elbows, 90 Degree Elbows, 45 Degree Elbows, 30 Degree Elbows, Equal Tee, Reducing Tee, Concentric Reducer, Eccentric Reducer, Lap Joint Stub End, Cap, Cross.
Stainless Steel Pipes.
Principal Design Features 317L is a low carbon version of 317 stainless. It possesses the same high strength and corrosion resistance and will produce stronger welds due to its low carbon content. Many users are shifting over to this alloy in lieu of 304 and 316 as availability and cost improves.
Applications Chemical and petrochemical process equipment, pulp and paper manufacturing and condensers in fossil and nuclear fueled power generation stations.
Machinability Low speeds and constant feeds will minimize this alloy's tendency to work harden. Tougher than 304 stainless with a long stringy chip, the use of chip breakers is recommended.
Welding All common fusion and resistance methods except oxyacetylene welding have proven successful. Use AWS E/ER 317L filler metal for best results.
Hot Working All common hot working processes are possible with this alloy. Heat to 2100-2300 F (1149-1260 C). Avoid working this material below 1700 F (927 C). For optimum corrosion resistance, a post-work annealing is recommended.
Cold Working Shearing, stamping, heading and drawing can be successfully performed . To remove internal stresses, a post-work annealing is recommended.
Annealing 1850-2050 F (1010-1121 C), followed by rapid cooling.
Hardening This alloy does not respond to heat treatment. Cold work will cause an increase in both hardness and strength.

Physical Data :

Density (lb / cu. in.) 0.29
Specific Gravity 7.9
Specific Heat (Btu/lb/Deg F - [32-212 Deg F]) 0.12
Electrical Resistivity (microhm-cm (at 68 Deg F)) 444
Melting Point (Deg F) 2550
Modulus of Elasticity Tension 28

Applications

Grade 317L stainless steel is widely used in the following applications:

  • Condensers in fossil
  • Pulp and paper manufacturing
  • Nuclear fueled power generation stations
  • Chemical and petrochemical process equipment.
  • Stainless Steel Pipes and Stainless Steel Tubes
  • Stainless Steel Pipe Fittings
  • Stainless Steel Flanges
  • Stainless Steel Forgings

Source: Yaang Pipe Industry Co., Limited (www.yaang.com)

Tel No:+86-18267732328 / Fax No :86-0577-56809281 / Email:sales@yaang.com
Address:Longwan District, Wenzhou, Zhejiang Province, China.

Copyright Notice © Yaang.com Yaang Pipe Industry Co., Limited All rights reserved.
Yaang Pipe Industry Co., Ltd. is an international supplier of piping solutions for flange, butt welding fittings, socket welding fittings and threaded fittings. Our products are widely used in different industrial fields, including oil and gas, chemical industry, petrochemical industry, power plant, pulp and paper industry, environmental and water conservancy engineering, engineering projects, etc.