ASME B16.9 ASTM B363 GR.WPT2 SMLS 90 Deg LR Elbow 2 Inch Sch40S
1) Size: 2 Inch (DN50)
3) Material: Titanium Grade WPT2 (UNS R50400)
China SMLS Elbow Manufacturer Yaang supplies ASME B16.9 ASTM B363 GR.WPT2 SMLS 90 Deg LR Elbow, 2 Inch, Sch40S.
Grade 2 Unalloyed Ti ("Pure") 50A alloy is hard to machine but can be successfully done using slow speeds, high coolant flow, and high feed rates. Tooling should be performed using tungsten carbide designations C1-C4 or cobalt type high speed tools.
Grade 2 Unalloyed Ti ("Pure") 50A alloy can be hot or cold formed using power brake, hydropress, stretch or drop hammer methods.
Weldability of grade 2 Unalloyed Ti ("Pure") 50A alloy is rated as good.
Annealing of this material can be performed by heating to 704°C (1299°F), and then held for 2 h, which should be followed by air cooling. In case intermediate stress relieving is required, the material has to be heated to 482°C (900°F) for 45 min.
Rough forging can be performed at 899°C (1650°F) and completed at 843°C (1550 °F).
|Titanium, Ti||≥ 98.9|
|Iron, Fe||≤ 0.30|
|Oxygen, O||≤ 0.25|
|Carbon, C||≤ 0.080|
|Nitrogen, N||≤ 0.030|
|Hydrogen, H||≤ 0.015|
|Density||4.51 g/cm||0.163 lb/in|
|Tensile strength||485 MPa||70300 psi|
|Yield strength||345 MPa||50000 psi|
|Elastic modulus||105 - 120 GPa||15200 - 17400 ksi|
|Elongation at break||28%||28%|
|Thermal expansion co-efficient (@0.000-100°C/32-212°F)||8.60 µm/m°C||4.78 µin/in°F|
|Thermal conductivity||21.97 W/mK||152.5 BTU in/hr.ft².°F|