99.0 Ti Ti Alloy
Production specification
Data center describes many of the common steel models, we can not determine the company's warehouse has all types of steel products inventory or raw materials.
Steel Pipe: 1 - 1300mm, also can be customed.
Pipe fitting Size: 1/8 inch - 80 inch (DN6 - DN2000)
Flange Size: DN6 - DN2000
Lenth: Any lenth based on the customer's requirement.
Chemical composition % of the ladle analysis of grade 99.0 Ti and Standards
Category Titanium Alloy
Class Wrought
Type Commercially Pure
Designations United States: ASTM B265 Grade4, ASTM B348 Grade4, ASTM B381 Grade4, MIL-T-9046, MIL-T-9047, AMS 4921, AMS 4901
Composition
Element Weight %
Ti 99.0
Mechanical Properties
Properties Conditions
T (°C) Treatment
Density (×1000 kg/m3) 4.51 25
Poisson's Ratio 0.34 25
Elastic Modulus (GPa) 104.1 25
Tensile Strength (Mpa) 310 315 more annealed
Yield Strength (Mpa) 172
Elongation (%) 25
Reduction in Area (%) 70
Hardness (HB) 265 25 annealed
Impact Strength (J)
(Charpy) 20 25 annealed
Thermal Properties
Properties Conditions
T (°C) Treatment
Thermal Expansion (10-6/ºC) 8.6 20-100 more
--------------------------------------------------------------------------------
Machining performance
99.0 Ti the mechanical properties of the report, the report provides detailed performance analysis and application.
--------------------------------------------------------------------------------
Principal Design Features
One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.
--------------------------------------------------------------------------------
Machinability
Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.
--------------------------------------------------------------------------------
Heat Treatment
CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.
--------------------------------------------------------------------------------
Welding
Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.
--------------------------------------------------------------------------------
Forging
Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.
--------------------------------------------------------------------------------
Hot tags:99.0 Ti tube plate, 99.0 Ti Pipe Fitting, 99.0 Ti flange, 99.0 Ti Angle Bar,99.0 Ti Valve,99.0 Ti forgings
stainless steel | mould steel | Heat resistant steel | Tool steel | Bearing steel | Spring steel | Alloy steel | Nickel base alloy and high nickel containing steels | Cementation steels | Free-cutting steels | Cold extrusion steels | Nitriding steels | Chain steels | Carbon steel | Ti Alloy | High temperature high strength alloy and high-temperature alloy | Low alloy high-temperature steel |
Titanium and Titanium Alloy Screws
Related hot word search:99.0 Ti Valve 99.0 Ti Ti Alloy,forging 99.0 Ti Ti Alloy,99.0 Ti Ti Alloy tube sheet,elbow 99.0 Ti Ti Alloy,99.0 Ti Ti Alloy flat bar,pipe 99.0 Ti Ti Alloy,99.0 Ti Ti Alloy Tee
Prev:99.1 Ti Ti Alloy
Next:SUS316N