- Ti-2.5Cu Ti Alloy Valve
- Ti-2.5Cu Ti Alloy Flange
- Ti-2.5Cu Ti Alloy pipe fitting
- Ti-2.5Cu Ti Alloy angle bar
- Ti-2.5Cu Ti Alloy pipe
Ti-2.5Cu Ti Alloy
Production specification
Data center describes many of the common steel models, we can not determine the company's warehouse has all types of steel products inventory or raw materials.
Steel Pipe: 1 - 1300mm, also can be customed.
Pipe fitting Size: 1/8 inch - 80 inch (DN6 - DN2000)
Flange Size: DN6 - DN2000
Lenth: Any lenth based on the customer's requirement.
Ti-2.5Cu Ti Alloy
Our advantages
Ti-2.5Cu properties and heat treatment forged piece, Including Ti-2.5Cu application and specifications, Including Ti-2.5Cu tube plate, Ti-2.5Cu Pipe Fitting, Ti-2.5Cu flange, Ti-2.5Cu Angle Bar,Ti-2.5Cu Valve,Ti-2.5Cu 3d bend.
--------------------------------------------------------------------------------
Introduction to Our Products:
Specialized high quality steel
We have the advantages of equipment, technologies and price
--------------------------------------------------------------------------------
Ti-2.5Cu has the following specifications:
Valve:
Diameter : 1mm-1300mm
Steel pipe:
Size:
OD: 9.5mm - 813mm
WT: 0.8mm - 34mm
Length: 1 - 13m, also can be customed.
Items |
seamless pipe & tube, pipe & tube |
|||
Standard |
ASTM, GB, DIN, AISI, etc |
|||
Outer Diameter |
Round pipe9.5mm--813mm |
|||
square |
12.7x12.7--200X200mm |
|||
rectangular |
20X40--150X200mm |
|||
Thickness |
0.8mm - 34mm |
|||
Length |
5.8m,6m, or as customers' request |
|||
Tolerance |
a) Outer Diameter: +/- 0.2mm |
|||
b) Thickness: +/- 0.02mm |
||||
c) Length: +/- 5mm |
||||
Surface |
180Grit, 320Grit, 400Grit Satin / Hairline |
|||
400Grit, 500Grit, 600Grit Mirror finish |
||||
Application |
Widely used in petroleum, Foodstuff, chemical industry, construction, electric power, nuclear energy, biotechnology, machinery, papermaking, shipbuilding, boiler fields, etc |
Pipe fitting:
Size: 1/8 inch - 80 inch (DN6 - DN2000) WT: Sch5s - Sch160XXS
Items |
Elbow,Equal Tee,Reducer Tee,Concentric Reducer,Eccentric Reducer,Cap,etc |
|
Standard |
ASME |
ANSI B16.9,ANSI B16.28,MSS-SP-75 |
DIN |
DIN2605,DIN2615, DIN2616, DIN2617, DIN28011 |
|
SGP |
JISB2313 |
|
EN |
EN10253-1 EN10253-2 |
|
Material |
ASME |
A234 WPB,A234 WP1,A234 WP5,A234,WP9, A234 WPB11,A234 WPB12,A234 WPB22,WP91, A420,WPHY42,WPHY52,WPHY60,WPHY65, WPHY70,WP304,WP304L,WP304H,WP316, WP316L,WP321,WP347,WP347H |
DIN |
ST37.0,ST35.8,ST45.8,S235JR,P235GH,P265GH, 10CrMo910,15CrMo,12Cr1MoV |
|
JIS |
JIS G3454,STPG370,TPG410 |
|
Surface |
Black paint/bright paint/Galvanized |
|
Marking |
As customer’s requirements |
Flange:
Product Name | Flange | |
Items | Plate, Welding Neck, Slip on, Blind, Lap joint, Threaded Flange | |
Standard | ANSI | ANSI B16.5 ASME B16.47 series A/B |
DIN | DIN | |
GOST | GOST 12820-80 | |
EN | EN1092-1:2002 | |
JIS | JIS B2220-2004, KS D3576, KS B6216 KS B1511-2007 JIS B2261; JIS B8210 | |
BS | BS4504 BS10 Table D/E | |
Material | ANSI | CS A105/SA 105NSS 304/304L, 316/316L Alloy Steel: WHPY45/52/65/80 |
DIN | CS RST37.2;S235JR SS 304/304L,316/316L | |
GOST | CS CT20;16MN;SS 304/304L,316/316L | |
EN | CS RST37.2;S235JR;C22.8SS 304/304L,316/316L | |
JIS | SS400,SF440 SS 304/304L, 316/316L | |
BS | CSRST37.2;S235JR;C22.8;Q235SS 304/304L,316/316L | |
Pressure | ANSI | Class 150, 300, 600, 900, 1500 2500lbs |
DIN | PN6,PN10,PN16,PN25,PN40,PN64,PN100 | |
GOST | PN6,PN10,PN16,PN25 | |
EN | PN6,PN10,PN16,PN25,PN40,PN64,PN100 | |
JIS | 1K,2K,5K,10K,16K,20K,30K,40K | |
BS | PN6,PN10,PN16,PN25,PN40,PN64,PN100 | |
Size | ANSI | 1/2” – 60” |
DIN | DN15-DN2000 | |
GOST | DN15-DN1600 | |
EN | DN15-DN2000 | |
JIS | 15A-1500A | |
BS | DN15-DN2000 | |
Coating | varnish, yellow paint, anti-rust oil, galvanizing etc | |
Usage | Used for the connection of all kinds of pipeline. | |
to convey the water, steam, air, gas and oil |
Length: Any length based on the customer's requirement.
--------------------------------------------------------------------------------
Chemical composition % of the ladle analysis of grade Ti-2.5Cu and Standards
Titanium IMI 230 (Ti-2.5Cu)
Categories: Metal; Nonferrous Metal; Titanium Alloy; Alpha/Near Alpha Titanium Alloy
Material Notes: Annealed; Aging increases Strength
Physical Properties Metric English Comments
Density 4.56 g/cc 0.165 lb/in³
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 620 MPa 89900 psi
Tensile Strength, Yield 480 MPa 69600 psi
Elongation at Break 24.0 % 24.0 %
Modulus of Elasticity 105 GPa 15200 ksi
Poissons Ratio 0.310 0.310 Typical for alpha titanium alloy.
Fatigue Strength 280 MPa
@# of Cycles 1.00e+7 40600 psi
@# of Cycles 1.00e+7
Shear Modulus 40.1 GPa 5820 ksi Calculated from typical values.
Electrical Properties Metric English Comments
Electrical Resistivity 0.0000650 ohm-cm 0.0000650 ohm-cm
Thermal Properties Metric English Comments
CTE, linear 9.02 µm/m-°C
@Temperature 20.0 - 100 °C 5.01 µin/in-°F
@Temperature 68.0 - 212 °F
9.10 µm/m-°C
@Temperature 20.0 - 300 °C 5.06 µin/in-°F
@Temperature 68.0 - 572 °F average
9.46 µm/m-°C
@Temperature 20.0 - 600 °C 5.26 µin/in-°F
@Temperature 68.0 - 1110 °F average
Specific Heat Capacity 0.525 J/g-°C 0.125 BTU/lb-°F Typical value for titanium alloys.
Thermal Conductivity 13.0 W/m-K 90.2 BTU-in/hr-ft²-°F
Beta Transus 895 °C 1640 °F
Component Elements Properties Metric English Comments
Carbon, C <= 0.0800 % <= 0.0800 %
Copper, Cu 2.00 - 3.00 % 2.00 - 3.00 %
Hydrogen, H <= 0.0100 % <= 0.0100 %
Iron, Fe <= 0.200 % <= 0.200 %
Nitrogen, N <= 0.0500 % <= 0.0500 %
Other, total <= 0.400 % <= 0.400 %
Oxygen, O <= 0.200 % <= 0.200 %
Titanium, Ti 96.06 - 98.0 % 96.06 - 98.0 % As Balance; Elemental Compostions per ASTM B265
Users viewing this material also viewed the following:
Titanium Ti-6Al-2Sn-4Zr-2Mo-0.1Si; Duplex Annealed
Titanium Ti-3Al-2.5V (Grade 9), alpha annealed
Titanium IMI 230 (Ti-2.5Cu), aged
Titanium Ti-5Al-2.5Sn (Grade 6)
Titanium 11 (Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si)
MTA231 / 14121
--------------------------------------------------------------------------------
Machining performance
Ti-2.5Cu the mechanical properties of the report, the report provides detailed performance analysis and application.
--------------------------------------------------------------------------------
Principal Design Features
One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.
--------------------------------------------------------------------------------
Machinability
Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.
--------------------------------------------------------------------------------
Heat Treatment
CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.
--------------------------------------------------------------------------------
Welding
Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.
--------------------------------------------------------------------------------
Forging
Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.
--------------------------------------------------------------------------------
Hot tags:Ti-2.5Cu tube plate, Ti-2.5Cu Pipe Fitting, Ti-2.5Cu flange, Ti-2.5Cu Angle Bar,Ti-2.5Cu Valve,Ti-2.5Cu forgings
stainless steel | mould steel | Heat resistant steel | Tool steel | Bearing steel | Spring steel | Alloy steel | Nickel base alloy and high nickel containing steels | Cementation steels | Free-cutting steels | Cold extrusion steels | Nitriding steels | Chain steels | Carbon steel | Ti Alloy | High temperature high strength alloy and high-temperature alloy | Low alloy high-temperature steel |
Related hot word search: Valve Ti-2.5Cu Ti Alloy,forging Ti-2.5Cu Ti Alloy,Ti-2.5Cu Ti Alloy tube sheet,elbow Ti-2.5Cu Ti Alloy,Ti-2.5Cu Ti Alloy flat bar,pipe Ti-2.5Cu Ti Alloy,Ti-2.5Cu Ti Alloy Tee
Prev:Ti-2.3Al-11Sn-5Zr-1Mo-0.2Si Ti Alloy
Next:Ti-5.5Al-4Sn-2Zr-1Mo-1Nd-0.25Si Ti Alloy