Ti-5Al-2.5Sn Grade 6 Ti Alloy
Production specification
Data center describes many of the common steel models, we can not determine the company's warehouse has all types of steel products inventory or raw materials.
Steel Pipe: 1 - 1300mm, also can be customed.
Pipe fitting Size: 1/8 inch - 80 inch (DN6 - DN2000)
Flange Size: DN6 - DN2000
Lenth: Any lenth based on the customer's requirement.
Ti-5Al-2.5Sn Grade 6 Ti Alloy
Our advantages
Ti-5Al-2.5Sn Grade 6 properties and heat treatment forged piece, Including Ti-5Al-2.5Sn Grade 6 application and specifications, Including Ti-5Al-2.5Sn Grade 6 tube plate, Ti-5Al-2.5Sn Grade 6 Pipe Fitting, Ti-5Al-2.5Sn Grade 6 flange, Ti-5Al-2.5Sn Grade 6 Angle Bar,Ti-5Al-2.5Sn Grade 6 Valve,Ti-5Al-2.5Sn Grade 6 3d bend.
--------------------------------------------------------------------------------
Introduction to Our Products:
Specialized high quality steel
We have the advantages of equipment, technologies and price
--------------------------------------------------------------------------------
Ti-5Al-2.5Sn Grade 6 has the following specifications:
Valve:
Diameter : 1mm-1300mm
Steel pipe:
Size:
OD: 9.5mm - 813mm
WT: 0.8mm - 34mm
Length: 1 - 13m, also can be customed.
Items |
seamless pipe & tube, pipe & tube |
|||
Standard |
ASTM, GB, DIN, AISI, etc |
|||
Outer Diameter |
Round pipe9.5mm--813mm |
|||
square |
12.7x12.7--200X200mm |
|||
rectangular |
20X40--150X200mm |
|||
Thickness |
0.8mm - 34mm |
|||
Length |
5.8m,6m, or as customers' request |
|||
Tolerance |
a) Outer Diameter: +/- 0.2mm |
|||
b) Thickness: +/- 0.02mm |
||||
c) Length: +/- 5mm |
||||
Surface |
180Grit, 320Grit, 400Grit Satin / Hairline |
|||
400Grit, 500Grit, 600Grit Mirror finish |
||||
Application |
Widely used in petroleum, Foodstuff, chemical industry, construction, electric power, nuclear energy, biotechnology, machinery, papermaking, shipbuilding, boiler fields, etc |
Pipe fitting:
Size: 1/8 inch - 80 inch (DN6 - DN2000) WT: Sch5s - Sch160XXS
Items |
Elbow,Equal Tee,Reducer Tee,Concentric Reducer,Eccentric Reducer,Cap,etc |
|
Standard |
ASME |
ANSI B16.9,ANSI B16.28,MSS-SP-75 |
DIN |
DIN2605,DIN2615, DIN2616, DIN2617, DIN28011 |
|
SGP |
JISB2313 |
|
EN |
EN10253-1 EN10253-2 |
|
Material |
ASME |
A234 WPB,A234 WP1,A234 WP5,A234,WP9, A234 WPB11,A234 WPB12,A234 WPB22,WP91, A420,WPHY42,WPHY52,WPHY60,WPHY65, WPHY70,WP304,WP304L,WP304H,WP316, WP316L,WP321,WP347,WP347H |
DIN |
ST37.0,ST35.8,ST45.8,S235JR,P235GH,P265GH, 10CrMo910,15CrMo,12Cr1MoV |
|
JIS |
JIS G3454,STPG370,TPG410 |
|
Surface |
Black paint/bright paint/Galvanized |
|
Marking |
As customer’s requirements |
Flange:
Product Name | Flange | |
Items | Plate, Welding Neck, Slip on, Blind, Lap joint, Threaded Flange | |
Standard | ANSI | ANSI B16.5 ASME B16.47 series A/B |
DIN | DIN | |
GOST | GOST 12820-80 | |
EN | EN1092-1:2002 | |
JIS | JIS B2220-2004, KS D3576, KS B6216 KS B1511-2007 JIS B2261; JIS B8210 | |
BS | BS4504 BS10 Table D/E | |
Material | ANSI | CS A105/SA 105NSS 304/304L, 316/316L Alloy Steel: WHPY45/52/65/80 |
DIN | CS RST37.2;S235JR SS 304/304L,316/316L | |
GOST | CS CT20;16MN;SS 304/304L,316/316L | |
EN | CS RST37.2;S235JR;C22.8SS 304/304L,316/316L | |
JIS | SS400,SF440 SS 304/304L, 316/316L | |
BS | CSRST37.2;S235JR;C22.8;Q235SS 304/304L,316/316L | |
Pressure | ANSI | Class 150, 300, 600, 900, 1500 2500lbs |
DIN | PN6,PN10,PN16,PN25,PN40,PN64,PN100 | |
GOST | PN6,PN10,PN16,PN25 | |
EN | PN6,PN10,PN16,PN25,PN40,PN64,PN100 | |
JIS | 1K,2K,5K,10K,16K,20K,30K,40K | |
BS | PN6,PN10,PN16,PN25,PN40,PN64,PN100 | |
Size | ANSI | 1/2” – 60” |
DIN | DN15-DN2000 | |
GOST | DN15-DN1600 | |
EN | DN15-DN2000 | |
JIS | 15A-1500A | |
BS | DN15-DN2000 | |
Coating | varnish, yellow paint, anti-rust oil, galvanizing etc | |
Usage | Used for the connection of all kinds of pipeline. | |
to convey the water, steam, air, gas and oil |
Length: Any length based on the customer's requirement.
--------------------------------------------------------------------------------
Chemical composition % of the ladle analysis of grade Ti-5Al-2.5Sn Grade 6 and Standards
Titanium Ti-5Al-2.5Sn (Grade 6)
Categories: Metal; Nonferrous Metal; Titanium Alloy; Alpha/Near Alpha Titanium Alloy
Material Notes: 1 other heat treatment of this alloy is in MatWeb.
Key Words: UNS R54520; Ti-5-2.5
Physical Properties Metric English Comments
Density 4.48 g/cc 0.162 lb/in³
Mechanical Properties Metric English Comments
Hardness, Brinell 320 320
Hardness, Knoop 363 363 Estimated from Rockwell C.
Hardness, Rockwell C 36 36
Hardness, Vickers 349 349 Estimated from Rockwell C.
Tensile Strength, Ultimate 861 MPa 125000 psi
Tensile Strength, Yield 827 MPa 120000 psi
Elongation at Break 15.0 % 15.0 %
Modulus of Elasticity 110 - 125 GPa 16000 - 18100 ksi
Compressive Yield Strength 830 MPa 120000 psi
Notched Tensile Strength 1240 MPa 180000 psi Kt (stress concentration factor) = 6.5
Ultimate Bearing Strength 1760 MPa 255000 psi e/D = 2
Bearing Yield Strength 1340 MPa 194000 psi e/D = 2
Poissons Ratio 0.310 0.310 Typical for alpha titanium alloy.
Charpy Impact 24.0 J 17.7 ft-lb V-notch
Fatigue Strength 290 MPa
@# of Cycles 1.00e+7 42100 psi
@# of Cycles 1.00e+7 Kt (stress concentration factor) = 2.4
380 MPa
@# of Cycles 1.00e+7 55100 psi
@# of Cycles 1.00e+7 unnotched
390 MPa
@# of Cycles 100000 56600 psi
@# of Cycles 100000 Kt (stress concentration factor) = 2.4
440 MPa
@# of Cycles 1.00e+6 63800 psi
@# of Cycles 1.00e+6 unnotched
530 MPa
@# of Cycles 100000 76900 psi
@# of Cycles 100000 Unnotched
Fracture Toughness 33.0 MPa-m½ 30.0 ksi-in½ K(ISCC)
96.0 MPa-m½ 87.4 ksi-in½ K(IC)
Shear Modulus 48.0 GPa 6960 ksi
Shear Strength 520 MPa 75400 psi Ultimate shear strength
Electrical Properties Metric English Comments
Electrical Resistivity 0.000160 ohm-cm 0.000160 ohm-cm
Thermal Properties Metric English Comments
CTE, linear 9.40 µm/m-°C
@Temperature 0.000 - 100 °C 5.22 µin/in-°F
@Temperature 32.0 - 212 °F
9.50 µm/m-°C
@Temperature 0.000 - 315 °C 5.28 µin/in-°F
@Temperature 32.0 - 599 °F average; unspecified heat treatment.
9.70 µm/m-°C
@Temperature 0.000 - 650 °C 5.39 µin/in-°F
@Temperature 32.0 - 1200 °F average
Specific Heat Capacity 0.530 J/g-°C 0.127 BTU/lb-°F 0.674 J/g-ºC at 315ºC
Thermal Conductivity 7.80 W/m-K 54.1 BTU-in/hr-ft²-°F 10.9 W/m-ºC at 315ºC
Melting Point <= 1590 °C <= 2890 °F Liquidus
Liquidus 1590 °C 2890 °F
Beta Transus 1040 - 1090 °C 1900 - 1990 °F
Component Elements Properties Metric English Comments
Aluminum, Al 4.00 - 6.00 % 4.00 - 6.00 %
Carbon, C <= 0.100 % <= 0.100 %
Hydrogen, H <= 0.0150 % <= 0.0150 %
Iron, Fe <= 0.500 % <= 0.500 %
Nitrogen, N <= 0.0300 % <= 0.0300 %
Other, each <= 0.0500 % <= 0.0500 %
Other, total <= 0.300 % <= 0.300 %
Oxygen, O <= 0.200 % <= 0.200 %
Tin, Sn 2.00 - 3.00 % 2.00 - 3.00 %
Titanium, Ti 89.855 - 94.0 % 89.855 - 94.0 % As Balance; Elemental Compostions per ASTM B265
Users viewing this material also viewed the following:
Titanium Ti-5Al-2.5Sn, ELI, Annealed
Titanium Ti-3Al-2.5V (Grade 9), alpha annealed
Titanium Ti-6Al-2Sn-4Zr-2Mo-0.1Si; Duplex Annealed
Titanium, Ti
Titanium Ti-6Al-4V (Grade 5), Annealed
MTA520 / 14127
--------------------------------------------------------------------------------
Machining performance
Ti-5Al-2.5Sn Grade 6 the mechanical properties of the report, the report provides detailed performance analysis and application.
--------------------------------------------------------------------------------
Principal Design Features
One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.
--------------------------------------------------------------------------------
Machinability
Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.
--------------------------------------------------------------------------------
Heat Treatment
CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.
--------------------------------------------------------------------------------
Welding
Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.
--------------------------------------------------------------------------------
Forging
Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.
--------------------------------------------------------------------------------
Hot tags:Ti-5Al-2.5Sn Grade 6 tube plate, Ti-5Al-2.5Sn Grade 6 Pipe Fitting, Ti-5Al-2.5Sn Grade 6 flange, Ti-5Al-2.5Sn Grade 6 Angle Bar,Ti-5Al-2.5Sn Grade 6 Valve,Ti-5Al-2.5Sn Grade 6 forgings
stainless steel | mould steel | Heat resistant steel | Tool steel | Bearing steel | Spring steel | Alloy steel | Nickel base alloy and high nickel containing steels | Cementation steels | Free-cutting steels | Cold extrusion steels | Nitriding steels | Chain steels | Carbon steel | Ti Alloy | High temperature high strength alloy and high-temperature alloy | Low alloy high-temperature steel |
Related hot word search:Ti-5Al-2.5Sn Grade Valve Ti-5Al-2.5Sn Grade 6 Ti Alloy,forging Ti-5Al-2.5Sn Grade 6 Ti Alloy,Ti-5Al-2.5Sn Grade 6 Ti Alloy tube sheet,elbow Ti-5Al-2.5Sn Grade 6 Ti Alloy,Ti-5Al-2.5Sn Grade 6 Ti Alloy flat bar,pipe Ti-5Al-2.5Sn Grade 6 Ti Alloy,Ti-5Al-2.5Sn Grade 6 Ti Alloy Tee
Prev:Ti-5Al-2Zr-2Mo-0.25Si Ti Alloy
Next:Ti-3Al-2.5V Grade 9 Ti Alloy