- Ti-6Al-2Nb-1Ta-0.8Mo Ti Alloy Valve
- Ti-6Al-2Nb-1Ta-0.8Mo Ti Alloy Flange
- Ti-6Al-2Nb-1Ta-0.8Mo Ti Alloy pipe fitting
- Ti-6Al-2Nb-1Ta-0.8Mo Ti Alloy angle bar
- Ti-6Al-2Nb-1Ta-0.8Mo Ti Alloy pipe
Ti-6Al-2Nb-1Ta-0.8Mo Ti Alloy
Production specification
Data center describes many of the common steel models, we can not determine the company's warehouse has all types of steel products inventory or raw materials.
Steel Pipe: 1 - 1300mm, also can be customed.
Pipe fitting Size: 1/8 inch - 80 inch (DN6 - DN2000)
Flange Size: DN6 - DN2000
Lenth: Any lenth based on the customer's requirement.
Ti-6Al-2Nb-1Ta-0.8Mo Ti Alloy
Our advantages
Ti-6Al-2Nb-1Ta-0.8Mo properties and heat treatment forged piece, Including Ti-6Al-2Nb-1Ta-0.8Mo application and specifications, Including Ti-6Al-2Nb-1Ta-0.8Mo tube plate, Ti-6Al-2Nb-1Ta-0.8Mo Pipe Fitting, Ti-6Al-2Nb-1Ta-0.8Mo flange, Ti-6Al-2Nb-1Ta-0.8Mo Angle Bar,Ti-6Al-2Nb-1Ta-0.8Mo Valve,Ti-6Al-2Nb-1Ta-0.8Mo 3d bend.
--------------------------------------------------------------------------------
Introduction to Our Products:
Specialized high quality steel
We have the advantages of equipment, technologies and price
--------------------------------------------------------------------------------
Ti-6Al-2Nb-1Ta-0.8Mo has the following specifications:
Valve:
Diameter : 1mm-1300mm
Steel pipe:
Size:
OD: 9.5mm - 813mm
WT: 0.8mm - 34mm
Length: 1 - 13m, also can be customed.
Items |
seamless pipe & tube, pipe & tube |
|||
Standard |
ASTM, GB, DIN, AISI, etc |
|||
Outer Diameter |
Round pipe9.5mm--813mm |
|||
square |
12.7x12.7--200X200mm |
|||
rectangular |
20X40--150X200mm |
|||
Thickness |
0.8mm - 34mm |
|||
Length |
5.8m,6m, or as customers' request |
|||
Tolerance |
a) Outer Diameter: +/- 0.2mm |
|||
b) Thickness: +/- 0.02mm |
||||
c) Length: +/- 5mm |
||||
Surface |
180Grit, 320Grit, 400Grit Satin / Hairline |
|||
400Grit, 500Grit, 600Grit Mirror finish |
||||
Application |
Widely used in petroleum, Foodstuff, chemical industry, construction, electric power, nuclear energy, biotechnology, machinery, papermaking, shipbuilding, boiler fields, etc |
Pipe fitting:
Size: 1/8 inch - 80 inch (DN6 - DN2000) WT: Sch5s - Sch160XXS
Items |
Elbow,Equal Tee,Reducer Tee,Concentric Reducer,Eccentric Reducer,Cap,etc |
|
Standard |
ASME |
ANSI B16.9,ANSI B16.28,MSS-SP-75 |
DIN |
DIN2605,DIN2615, DIN2616, DIN2617, DIN28011 |
|
SGP |
JISB2313 |
|
EN |
EN10253-1 EN10253-2 |
|
Material |
ASME |
A234 WPB,A234 WP1,A234 WP5,A234,WP9, A234 WPB11,A234 WPB12,A234 WPB22,WP91, A420,WPHY42,WPHY52,WPHY60,WPHY65, WPHY70,WP304,WP304L,WP304H,WP316, WP316L,WP321,WP347,WP347H |
DIN |
ST37.0,ST35.8,ST45.8,S235JR,P235GH,P265GH, 10CrMo910,15CrMo,12Cr1MoV |
|
JIS |
JIS G3454,STPG370,TPG410 |
|
Surface |
Black paint/bright paint/Galvanized |
|
Marking |
As customer’s requirements |
Flange:
Product Name | Flange | |
Items | Plate, Welding Neck, Slip on, Blind, Lap joint, Threaded Flange | |
Standard | ANSI | ANSI B16.5 ASME B16.47 series A/B |
DIN | DIN | |
GOST | GOST 12820-80 | |
EN | EN1092-1:2002 | |
JIS | JIS B2220-2004, KS D3576, KS B6216 KS B1511-2007 JIS B2261; JIS B8210 | |
BS | BS4504 BS10 Table D/E | |
Material | ANSI | CS A105/SA 105NSS 304/304L, 316/316L Alloy Steel: WHPY45/52/65/80 |
DIN | CS RST37.2;S235JR SS 304/304L,316/316L | |
GOST | CS CT20;16MN;SS 304/304L,316/316L | |
EN | CS RST37.2;S235JR;C22.8SS 304/304L,316/316L | |
JIS | SS400,SF440 SS 304/304L, 316/316L | |
BS | CSRST37.2;S235JR;C22.8;Q235SS 304/304L,316/316L | |
Pressure | ANSI | Class 150, 300, 600, 900, 1500 2500lbs |
DIN | PN6,PN10,PN16,PN25,PN40,PN64,PN100 | |
GOST | PN6,PN10,PN16,PN25 | |
EN | PN6,PN10,PN16,PN25,PN40,PN64,PN100 | |
JIS | 1K,2K,5K,10K,16K,20K,30K,40K | |
BS | PN6,PN10,PN16,PN25,PN40,PN64,PN100 | |
Size | ANSI | 1/2” – 60” |
DIN | DN15-DN2000 | |
GOST | DN15-DN1600 | |
EN | DN15-DN2000 | |
JIS | 15A-1500A | |
BS | DN15-DN2000 | |
Coating | varnish, yellow paint, anti-rust oil, galvanizing etc | |
Usage | Used for the connection of all kinds of pipeline. | |
to convey the water, steam, air, gas and oil |
Length: Any length based on the customer's requirement.
--------------------------------------------------------------------------------
Chemical composition % of the ladle analysis of grade Ti-6Al-2Nb-1Ta-0.8Mo and Standards
Titanium Ti-6Al-2Nb-1Ta-0.8Mo (Ti-621/0.8), as-rolled
Categories: Metal; Nonferrous Metal; Titanium Alloy; Alpha/Near Alpha Titanium Alloy
Material Notes: As-rolled from above Beta Transus. Alpha Alloy.
3 other heat treatments of this alloy are in MatWeb.
Key Words: Ti-621/0.8; UNS R56210; Ti-6211
Physical Properties Metric English Comments
Density 4.48 g/cc 0.162 lb/in³
Mechanical Properties Metric English Comments
Hardness, Brinell 290 290 Estimated from Rockwell C.
Hardness, Knoop 315 315 Estimated from Rockwell C.
Hardness, Rockwell C 30 30
Hardness, Vickers 304 304 Estimated from Rockwell C.
Tensile Strength, Ultimate 830 MPa 120000 psi
Tensile Strength, Yield 760 MPa 110000 psi
Elongation at Break 10.0 % 10.0 %
Reduction of Area 28.0 % 28.0 % Average of Longitudinal and Transverse
Modulus of Elasticity 117 GPa 17000 ksi In Tension
Compressive Yield Strength 820 MPa 119000 psi
Compressive Modulus 126 GPa 18300 ksi
Poissons Ratio 0.310 0.310
Charpy Impact 37.0 J 27.3 ft-lb V-notch
Shear Modulus 44.7 GPa 6480 ksi Calculated
Electrical Properties Metric English Comments
Electrical Resistivity 0.000160 ohm-cm 0.000160 ohm-cm
Thermal Properties Metric English Comments
CTE, linear 9.00 µm/m-°C
@Temperature 20.0 - 650 °C 5.00 µin/in-°F
@Temperature 68.0 - 1200 °F average
9.20 µm/m-°C
@Temperature 20.0 - 93.0 °C 5.11 µin/in-°F
@Temperature 68.0 - 199 °F annealed
Specific Heat Capacity 0.552 J/g-°C 0.132 BTU/lb-°F
Thermal Conductivity 6.40 W/m-K 44.4 BTU-in/hr-ft²-°F
Melting Point <= 1650 °C <= 3000 °F Liquidus
Liquidus 1650 °C 3000 °F
Beta Transus 1110 °C 2030 °F
Component Elements Properties Metric English Comments
Aluminum, Al 6.0 % 6.0 %
Molybdenum, Mo 0.80 % 0.80 %
Niobium, Nb (Columbium, Cb) 2.0 % 2.0 %
Tantalum, Ta 1.0 % 1.0 %
Titanium, Ti 90.0 % 90.0 %
Users viewing this material also viewed the following:
Titanium Ti-6Al-2Sn-4Zr-2Mo-0.1Si; Duplex Annealed
Titanium Ti-6Al-2Nb-1Ta-0.8Mo (Ti-621/0.8), Alpha-Annealed
Titanium 11 (Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si)
Titanium Ti-6Al-2Nb-1Ta-0.8Mo (Ti-621/0.8), STA-1
Titanium Ti-6Al-2Nb-1Ta-1Mo
MTA181 / 14117
--------------------------------------------------------------------------------
Machining performance
Ti-6Al-2Nb-1Ta-0.8Mo the mechanical properties of the report, the report provides detailed performance analysis and application.
--------------------------------------------------------------------------------
Principal Design Features
One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.
--------------------------------------------------------------------------------
Machinability
Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.
--------------------------------------------------------------------------------
Heat Treatment
CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.
--------------------------------------------------------------------------------
Welding
Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.
--------------------------------------------------------------------------------
Forging
Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.
--------------------------------------------------------------------------------
Hot tags:Ti-6Al-2Nb-1Ta-0.8Mo tube plate, Ti-6Al-2Nb-1Ta-0.8Mo Pipe Fitting, Ti-6Al-2Nb-1Ta-0.8Mo flange, Ti-6Al-2Nb-1Ta-0.8Mo Angle Bar,Ti-6Al-2Nb-1Ta-0.8Mo Valve,Ti-6Al-2Nb-1Ta-0.8Mo forgings
stainless steel | mould steel | Heat resistant steel | Tool steel | Bearing steel | Spring steel | Alloy steel | Nickel base alloy and high nickel containing steels | Cementation steels | Free-cutting steels | Cold extrusion steels | Nitriding steels | Chain steels | Carbon steel | Ti Alloy | High temperature high strength alloy and high-temperature alloy | Low alloy high-temperature steel |
Related hot word search:Ti-6Al-2Nb-1Ta-0.8Mo Ti Valve Ti-6Al-2Nb-1Ta-0.8Mo Ti Alloy,forging Ti-6Al-2Nb-1Ta-0.8Mo Ti Alloy,Ti-6Al-2Nb-1Ta-0.8Mo Ti Alloy tube sheet,elbow Ti-6Al-2Nb-1Ta-0.8Mo Ti Alloy,Ti-6Al-2Nb-1Ta-0.8Mo Ti Alloy flat bar,pipe Ti-6Al-2Nb-1Ta-0.8Mo Ti Alloy,Ti-6Al-2Nb-1Ta-0.8Mo Ti Alloy Tee
Prev:Ti-621/0.8 Ti Alloy
Next:Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si Ti Alloy