UNS R56400 Ti Alloy
Production specification
Data center describes many of the common steel models, we can not determine the company's warehouse has all types of steel products inventory or raw materials.
Steel Pipe: 1 - 1300mm, also can be customed.
Pipe fitting Size: 1/8 inch - 80 inch (DN6 - DN2000)
Flange Size: DN6 - DN2000
Lenth: Any lenth based on the customer's requirement.
UNS R56400 Ti Alloy
Our advantages
UNS R56400 properties and heat treatment forged piece, Including UNS R56400 application and specifications, Including UNS R56400 tube plate, UNS R56400 Pipe Fitting, UNS R56400 flange, UNS R56400 Angle Bar,UNS R56400 Valve,UNS R56400 3d bend.
--------------------------------------------------------------------------------
Introduction to Our Products:
Specialized high quality steel
We have the advantages of equipment, technologies and price
--------------------------------------------------------------------------------
UNS R56400 has the following specifications:
Valve:
Diameter : 1mm-1300mm
Steel pipe:
Size:
OD: 9.5mm - 813mm
WT: 0.8mm - 34mm
Length: 1 - 13m, also can be customed.
Items |
seamless pipe & tube, pipe & tube |
|||
Standard |
ASTM, GB, DIN, AISI, etc |
|||
Outer Diameter |
Round pipe9.5mm--813mm |
|||
square |
12.7x12.7--200X200mm |
|||
rectangular |
20X40--150X200mm |
|||
Thickness |
0.8mm - 34mm |
|||
Length |
5.8m,6m, or as customers' request |
|||
Tolerance |
a) Outer Diameter: +/- 0.2mm |
|||
b) Thickness: +/- 0.02mm |
||||
c) Length: +/- 5mm |
||||
Surface |
180Grit, 320Grit, 400Grit Satin / Hairline |
|||
400Grit, 500Grit, 600Grit Mirror finish |
||||
Application |
Widely used in petroleum, Foodstuff, chemical industry, construction, electric power, nuclear energy, biotechnology, machinery, papermaking, shipbuilding, boiler fields, etc |
Pipe fitting:
Size: 1/8 inch - 80 inch (DN6 - DN2000) WT: Sch5s - Sch160XXS
Items |
Elbow,Equal Tee,Reducer Tee,Concentric Reducer,Eccentric Reducer,Cap,etc |
|
Standard |
ASME |
ANSI B16.9,ANSI B16.28,MSS-SP-75 |
DIN |
DIN2605,DIN2615, DIN2616, DIN2617, DIN28011 |
|
SGP |
JISB2313 |
|
EN |
EN10253-1 EN10253-2 |
|
Material |
ASME |
A234 WPB,A234 WP1,A234 WP5,A234,WP9, A234 WPB11,A234 WPB12,A234 WPB22,WP91, A420,WPHY42,WPHY52,WPHY60,WPHY65, WPHY70,WP304,WP304L,WP304H,WP316, WP316L,WP321,WP347,WP347H |
DIN |
ST37.0,ST35.8,ST45.8,S235JR,P235GH,P265GH, 10CrMo910,15CrMo,12Cr1MoV |
|
JIS |
JIS G3454,STPG370,TPG410 |
|
Surface |
Black paint/bright paint/Galvanized |
|
Marking |
As customer’s requirements |
Flange:
Product Name | Flange | |
Items | Plate, Welding Neck, Slip on, Blind, Lap joint, Threaded Flange | |
Standard | ANSI | ANSI B16.5 ASME B16.47 series A/B |
DIN | DIN | |
GOST | GOST 12820-80 | |
EN | EN1092-1:2002 | |
JIS | JIS B2220-2004, KS D3576, KS B6216 KS B1511-2007 JIS B2261; JIS B8210 | |
BS | BS4504 BS10 Table D/E | |
Material | ANSI | CS A105/SA 105NSS 304/304L, 316/316L Alloy Steel: WHPY45/52/65/80 |
DIN | CS RST37.2;S235JR SS 304/304L,316/316L | |
GOST | CS CT20;16MN;SS 304/304L,316/316L | |
EN | CS RST37.2;S235JR;C22.8SS 304/304L,316/316L | |
JIS | SS400,SF440 SS 304/304L, 316/316L | |
BS | CSRST37.2;S235JR;C22.8;Q235SS 304/304L,316/316L | |
Pressure | ANSI | Class 150, 300, 600, 900, 1500 2500lbs |
DIN | PN6,PN10,PN16,PN25,PN40,PN64,PN100 | |
GOST | PN6,PN10,PN16,PN25 | |
EN | PN6,PN10,PN16,PN25,PN40,PN64,PN100 | |
JIS | 1K,2K,5K,10K,16K,20K,30K,40K | |
BS | PN6,PN10,PN16,PN25,PN40,PN64,PN100 | |
Size | ANSI | 1/2” – 60” |
DIN | DN15-DN2000 | |
GOST | DN15-DN1600 | |
EN | DN15-DN2000 | |
JIS | 15A-1500A | |
BS | DN15-DN2000 | |
Coating | varnish, yellow paint, anti-rust oil, galvanizing etc | |
Usage | Used for the connection of all kinds of pipeline. | |
to convey the water, steam, air, gas and oil |
Length: Any length based on the customer's requirement.
--------------------------------------------------------------------------------
Chemical composition % of the ladle analysis of grade UNS R56400 and Standards
Allvac® 6-4 Titanium Alloy, Heat Treatment: 704°C (1300°F) Anneal
Categories: Metal; Nonferrous Metal; Titanium Alloy; Alpha/Beta Titanium Alloy
Material Notes: Data provided by Allvac.
Applications: Blades, discs, rings, airframe, fasteners, components. Vessels, cases, hubs, forgings. Standard, rotor/premium grades.
Key Words: UNS R56400; AMS 4906, 4920, 4928, 4965, 4967; MIL-T-9047, -81556, Ti-6Al-4V; Ti-6-4; ASTM B 348, B 381, F 1472; Allvac, an Allegheny Teledyne Company
Physical Properties Metric English Comments
Density 4.43 g/cc 0.160 lb/in³
Mechanical Properties Metric English Comments
Hardness, Brinell 304 304 Estimated from Rockwell C value for Brinell test with 3000 kg load/10 mm diameter ball
Hardness, Knoop 330 330 Estimated from Rockwell C value.
Hardness, Rockwell C 32 32
Hardness, Vickers 318 318 Estimated from Rockwell C value.
Tensile Strength, Ultimate 931 MPa 135000 psi
Tensile Strength, Yield 862 MPa
@Strain 0.200 % 125000 psi
@Strain 0.200 %
Elongation at Break 15.0 % 15.0 %
Reduction of Area 30.0 % 30.0 %
Component Elements Properties Metric English Comments
Aluminum, Al 6.0 % 6.0 %
Carbon, C <= 0.10 % <= 0.10 %
Hydrogen, H <= 0.015 % <= 0.015 %
Iron, Fe 0.20 % 0.20 %
Nitrogen, N 0.030 % 0.030 %
Oxygen, O <= 0.20 % <= 0.20 %
Titanium, Ti 89.0 % 89.0 % as balance
Vanadium, V 4.0 % 4.0 %
Users viewing this material also viewed the following:
Titanium Ti-6Al-4V (Grade 5), Annealed
Titanium Ti-6Al-4V (Grade 5), STA
Allvac® 6-4ELI Titanium Alloy, Heat Treatment: 704°C (1300°F) Anneal
Titanium Ti-6Al-4V (Grade 5), Annealed Bar
Titanium Ti-6Al-4V (Grade 5), STA Bar
NALL45 / 14795
--------------------------------------------------------------------------------
Machining performance
UNS R56400 the mechanical properties of the report, the report provides detailed performance analysis and application.
--------------------------------------------------------------------------------
Principal Design Features
One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.
--------------------------------------------------------------------------------
Machinability
Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.
--------------------------------------------------------------------------------
Heat Treatment
CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.
--------------------------------------------------------------------------------
Welding
Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.
--------------------------------------------------------------------------------
Forging
Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.
--------------------------------------------------------------------------------
Hot tags:UNS R56400 tube plate, UNS R56400 Pipe Fitting, UNS R56400 flange, UNS R56400 Angle Bar,UNS R56400 Valve,UNS R56400 forgings
stainless steel | mould steel | Heat resistant steel | Tool steel | Bearing steel | Spring steel | Alloy steel | Nickel base alloy and high nickel containing steels | Cementation steels | Free-cutting steels | Cold extrusion steels | Nitriding steels | Chain steels | Carbon steel | Ti Alloy | High temperature high strength alloy and high-temperature alloy | Low alloy high-temperature steel |
Related hot word search:UNS R56400 Valve UNS R56400 Ti Alloy,forging UNS R56400 Ti Alloy,UNS R56400 Ti Alloy tube sheet,elbow UNS R56400 Ti Alloy,UNS R56400 Ti Alloy flat bar,pipe UNS R56400 Ti Alloy,UNS R56400 Ti Alloy Tee
Prev:MIL-T-9047 Ti Alloy
Next:UNS R54520 Ti Alloy