Ti 10-2-3 Ti Alloy
Production specification
Data center describes many of the common steel models, we can not determine the company's warehouse has all types of steel products inventory or raw materials.
Steel Pipe: 1 - 1300mm, also can be customed.
Pipe fitting Size: 1/8 inch - 80 inch (DN6 - DN2000)
Flange Size: DN6 - DN2000
Lenth: Any lenth based on the customer's requirement.
Ti 10-2-3 Ti Alloy
Our advantages
Ti 10-2-3 properties and heat treatment forged piece, Including Ti 10-2-3 application and specifications, Including Ti 10-2-3 tube plate, Ti 10-2-3 Pipe Fitting, Ti 10-2-3 flange, Ti 10-2-3 Angle Bar,Ti 10-2-3 Valve,Ti 10-2-3 3d bend.
--------------------------------------------------------------------------------
Introduction to Our Products:
Specialized high quality steel
We have the advantages of equipment, technologies and price
--------------------------------------------------------------------------------
Ti 10-2-3 has the following specifications:
Valve:
Diameter : 1mm-1300mm
Steel pipe:
Size:
OD: 9.5mm - 813mm
WT: 0.8mm - 34mm
Length: 1 - 13m, also can be customed.
Items |
seamless pipe & tube, pipe & tube |
|||
Standard |
ASTM, GB, DIN, AISI, etc |
|||
Outer Diameter |
Round pipe9.5mm--813mm |
|||
square |
12.7x12.7--200X200mm |
|||
rectangular |
20X40--150X200mm |
|||
Thickness |
0.8mm - 34mm |
|||
Length |
5.8m,6m, or as customers' request |
|||
Tolerance |
a) Outer Diameter: +/- 0.2mm |
|||
b) Thickness: +/- 0.02mm |
||||
c) Length: +/- 5mm |
||||
Surface |
180Grit, 320Grit, 400Grit Satin / Hairline |
|||
400Grit, 500Grit, 600Grit Mirror finish |
||||
Application |
Widely used in petroleum, Foodstuff, chemical industry, construction, electric power, nuclear energy, biotechnology, machinery, papermaking, shipbuilding, boiler fields, etc |
Pipe fitting:
Size: 1/8 inch - 80 inch (DN6 - DN2000) WT: Sch5s - Sch160XXS
Items |
Elbow,Equal Tee,Reducer Tee,Concentric Reducer,Eccentric Reducer,Cap,etc |
|
Standard |
ASME |
ANSI B16.9,ANSI B16.28,MSS-SP-75 |
DIN |
DIN2605,DIN2615, DIN2616, DIN2617, DIN28011 |
|
SGP |
JISB2313 |
|
EN |
EN10253-1 EN10253-2 |
|
Material |
ASME |
A234 WPB,A234 WP1,A234 WP5,A234,WP9, A234 WPB11,A234 WPB12,A234 WPB22,WP91, A420,WPHY42,WPHY52,WPHY60,WPHY65, WPHY70,WP304,WP304L,WP304H,WP316, WP316L,WP321,WP347,WP347H |
DIN |
ST37.0,ST35.8,ST45.8,S235JR,P235GH,P265GH, 10CrMo910,15CrMo,12Cr1MoV |
|
JIS |
JIS G3454,STPG370,TPG410 |
|
Surface |
Black paint/bright paint/Galvanized |
|
Marking |
As customer’s requirements |
Flange:
Product Name | Flange | |
Items | Plate, Welding Neck, Slip on, Blind, Lap joint, Threaded Flange | |
Standard | ANSI | ANSI B16.5 ASME B16.47 series A/B |
DIN | DIN | |
GOST | GOST 12820-80 | |
EN | EN1092-1:2002 | |
JIS | JIS B2220-2004, KS D3576, KS B6216 KS B1511-2007 JIS B2261; JIS B8210 | |
BS | BS4504 BS10 Table D/E | |
Material | ANSI | CS A105/SA 105NSS 304/304L, 316/316L Alloy Steel: WHPY45/52/65/80 |
DIN | CS RST37.2;S235JR SS 304/304L,316/316L | |
GOST | CS CT20;16MN;SS 304/304L,316/316L | |
EN | CS RST37.2;S235JR;C22.8SS 304/304L,316/316L | |
JIS | SS400,SF440 SS 304/304L, 316/316L | |
BS | CSRST37.2;S235JR;C22.8;Q235SS 304/304L,316/316L | |
Pressure | ANSI | Class 150, 300, 600, 900, 1500 2500lbs |
DIN | PN6,PN10,PN16,PN25,PN40,PN64,PN100 | |
GOST | PN6,PN10,PN16,PN25 | |
EN | PN6,PN10,PN16,PN25,PN40,PN64,PN100 | |
JIS | 1K,2K,5K,10K,16K,20K,30K,40K | |
BS | PN6,PN10,PN16,PN25,PN40,PN64,PN100 | |
Size | ANSI | 1/2” – 60” |
DIN | DN15-DN2000 | |
GOST | DN15-DN1600 | |
EN | DN15-DN2000 | |
JIS | 15A-1500A | |
BS | DN15-DN2000 | |
Coating | varnish, yellow paint, anti-rust oil, galvanizing etc | |
Usage | Used for the connection of all kinds of pipeline. | |
to convey the water, steam, air, gas and oil |
Length: Any length based on the customer's requirement.
--------------------------------------------------------------------------------
Chemical composition % of the ladle analysis of grade Ti 10-2-3 and Standards
Titanium Ti-10V-2Fe-3Al (Ti 10-2-3) Solution Treated 850°C (1560°F)
Categories: Metal; Nonferrous Metal; Titanium Alloy; Beta Titanium Alloy
Material Notes: 5 other heat treatments of this alloy are in MatWeb.
Key Words: KS 10-2-3; Ti 10-2-3; TIMETAL 10-2-3
Physical Properties Metric English Comments
Density 4.65 g/cc 0.168 lb/in³
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 1000 MPa 145000 psi
Tensile Strength, Yield 930 MPa 135000 psi
Elongation at Break 17.0 % 17.0 %
Modulus of Elasticity 110 GPa 16000 ksi unspecified heat treatment
Poissons Ratio 0.330 0.330 Typical for beta titanium alloy.
Fracture Toughness 110 MPa-m½ 100 ksi-in½ K(IC)
Shear Modulus 41.0 GPa 5950 ksi
Electrical Properties Metric English Comments
Electrical Resistivity 0.000150 ohm-cm 0.000150 ohm-cm Estimated from similar high-V-stabilized beta titanium alloys.
Thermal Properties Metric English Comments
CTE, linear 9.70 µm/m-°C
@Temperature 20.0 - 100 °C 5.39 µin/in-°F
@Temperature 68.0 - 212 °F
9.70 µm/m-°C
@Temperature 20.0 - 425 °C 5.39 µin/in-°F
@Temperature 68.0 - 797 °F average after ST 760ºC; Age 525ºC
Specific Heat Capacity 0.525 J/g-°C 0.125 BTU/lb-°F Typical value for titanium alloys.
Thermal Conductivity 7.80 W/m-K 54.1 BTU-in/hr-ft²-°F Estimated from similar high-V-stabilized beta titanium alloys.
Maximum Service Temperature, Air 315 °C 599 °F
Beta Transus 760 °C 1400 °F
Component Elements Properties Metric English Comments
Aluminum, Al 2.60 - 3.40 % 2.60 - 3.40 %
Carbon, C <= 0.0500 % <= 0.0500 %
Hydrogen, H <= 0.0150 % <= 0.0150 %
Iron, Fe 1.60 - 2.20 % 1.60 - 2.20 %
Nitrogen, N <= 0.0500 % <= 0.0500 %
Other, each <= 0.100 % <= 0.100 %
Other, total <= 0.300 % <= 0.300 %
Oxygen, O <= 0.130 % <= 0.130 %
Titanium, Ti 82.855 - 86.8 % 82.855 - 86.8 % As Balance; Elemental Compostions per ASTM B265
Vanadium, V 9.00 - 11.0 % 9.00 - 11.0 %
Users viewing this material also viewed the following:
Titanium Ti-10V-2Fe-3Al (Ti 10-2-3) ST 760°C, Aged 385°C
Titanium Ti-10V-2Fe-3Al (Ti 10-2-3) ST 760°C; Age 525°C (980°F)
Titanium Ti-10V-2Fe-3Al (Ti 10-2-3) ST 815°C, Anneal 620°C
Titanium Ti-10V-2Fe-3Al (Ti 10-2-3) ST 730°C; overage 580°C
Titanium Ti-10V-2Fe-3Al (Ti 10-2-3), Anneal 1 hr. 760°C
MTB020 / 14144
--------------------------------------------------------------------------------
Machining performance
Ti 10-2-3 the mechanical properties of the report, the report provides detailed performance analysis and application.
--------------------------------------------------------------------------------
Principal Design Features
One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.
--------------------------------------------------------------------------------
Machinability
Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.
--------------------------------------------------------------------------------
Heat Treatment
CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.
--------------------------------------------------------------------------------
Welding
Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.
--------------------------------------------------------------------------------
Forging
Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.
--------------------------------------------------------------------------------
Hot tags:Ti 10-2-3 tube plate, Ti 10-2-3 Pipe Fitting, Ti 10-2-3 flange, Ti 10-2-3 Angle Bar,Ti 10-2-3 Valve,Ti 10-2-3 forgings
stainless steel | mould steel | Heat resistant steel | Tool steel | Bearing steel | Spring steel | Alloy steel | Nickel base alloy and high nickel containing steels | Cementation steels | Free-cutting steels | Cold extrusion steels | Nitriding steels | Chain steels | Carbon steel | Ti Alloy | High temperature high strength alloy and high-temperature alloy | Low alloy high-temperature steel |
Related hot word search:Ti 10-2-3 Valve Ti 10-2-3 Ti Alloy,forging Ti 10-2-3 Ti Alloy,Ti 10-2-3 Ti Alloy tube sheet,elbow Ti 10-2-3 Ti Alloy,Ti 10-2-3 Ti Alloy flat bar,pipe Ti 10-2-3 Ti Alloy,Ti 10-2-3 Ti Alloy Tee
Prev:Ti-5-5-2-3 Ti Alloy
Next:Titanium 1100 Ti Alloy